Triaryl Amine Thick Layer Doped with Metal Amides for use as HIL for an Organic Light-Emitting Diode (OLED)

ABSTRACT

The present invention relates to a hole injection layer for an OLED comprising a triarylamine compound doped with a charge neutral metal amide compound, characterized in that the hole injection layer has a thickness of at least about ≥20 nm to about ≤1000 nm and the charge neutral metal amide compound has the Formula Ia.

The present invention relates to a triaryl amine thick layer doped with a metal amide for use as hole injection layer (HIL) for an Organic light-emitting diode (OLED), and a method of manufacturing Organic light-emitting diode (OLED) comprising the triaryl amine thick layer HIL doped with a metal amide.

DESCRIPTION OF THE RELATED ART

Organic solar cell as disclosed in EP 1 209 708 A1 having the general structure:

substrate+EM/HTM/dye/SOL/EM, or substrate+EM/SOL/dye/HTM/EM, or substrate+EM/HTM/SOL/EM, in which EM is the electrode material that may be a transparent conductive oxide (TCO) or metal, with at least one of the EM layer(s) of the cell being a TCO, HTM is the hole transport material, SOL is a semiconducting oxide layer, “dye” is a suitable dye, and the SOL layer is vapor deposited.

US 2013/0330632 A1 refers to electrochemical devices comprising complexes of cobalt comprising at least one ligand with a 5- or six membered, N-containing heteroring. The complex are useful as p- and n-dopants, as over of electrochemical devices, in particular in organic semiconductors. The complexes are further useful as over-discharge prevention and overvoltage protection agents.

Organic light-emitting diodes (OLEDs), which are self-emitting devices, have a wide viewing angle, excellent contrast, quick response, high brightness, excellent driving voltage characteristics, and color reproduction. A typical OLED includes an anode, a hole injection layer (HIL), a hole transport layer (HTL), an emission layer (EML), an electron transport layer (ETL), and a cathode, which are sequentially stacked on a substrate. In this regard, the HIL, the HTL, the EML, and the ETL are thin films formed from organic compounds.

When a voltage is applied to the anode and the cathode, holes injected from the anode move to the EML, via the HIL and HTL, and electrons injected from the cathode move to the EML, via the ETL. The holes and electrons recombine in the EML to generate excitons. When the excitons drop from an excited state to a ground state, light is emitted. The injection and flow of holes and electrons should be balanced, so that an OLED having the above-described structure has excellent efficiency and/or a long lifetime.

Dipyrazino[2,3-f:2′,3′-h]quinoxaline-2,3,6,7,10,11-hexacarbonitrile (CNHAT (CAS 105598-27-4)) having the Formula A, which is typically used as hole injection layer has several drawbacks.

For example, if the HOMO level of the hole transport layer of an OLED comprising a CNHAT HIL-layer is further away from the vacuum level, the voltage of the OLED is too high. Further, effective hole injection even into very deep HOMO HTLs, that means the HOMO is further away from vacuum level, is not sufficiently achieved.

Efficient hole injection into very deep HOMO levels enables the use of high efficiency emission layers, in particular phosphorescent blue and green emitters and emission which relies on TADF (thermally activated delayed fluorescence).

Thus, it is still desired to provide a hole injection layer material that more effectively promotes the hole injection over a broader range of HOMO levels to vacuum level from the HIL-layer into the hole transport layer (HTL).

Additionally, it is still desired to provide a thick hole injection layer material that provides an effective smoothing layer and thereby provides a pinhole-free basis for deposition of subsequent layers, so that defect-free OLEDs can be obtained even if the substrate is non-uniform.

SUMMARY

Aspects of the present invention provide a method of reducing the drive voltage and improving the voltage stability over time, especially for blue emitting OLEDs, and/or the external quantum efficiency EQE, for top and/or bottom emission organic light-emitting diodes (OLED). The invention relates to a hole injection layer (HIL) for use for an Organic light-emitting diode (OLED). The invention relates further to an organic light-emitting diode (OLED) comprising an anode, a hole injection layer (HIL), a hole transport layer (HTL), an emission layer (EML), optional a hole blocking layer (HBL), optional an electron transport layer (ETL), optional an electron injection layer (EIL), and a cathode as well as a method of manufacturing the same.

According to an aspect of the present invention, there is provided a hole injection layer (HIL) for an OLED comprising a triarylamine compound doped with a charge neutral metal amide compound, wherein the hole injection layer has a thickness of at least about ≥20 nm to about ≤1000 nm and the charge neutral metal amide compound has the Formula Ia:

-   -   wherein:     -   G=halide, O, alkoxylate or amine of Formula IIa to IIe:

-   -   R¹ to R⁵ are independently selected from the group comprising H,         C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to         C₁₂ substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂         substituted heteroaryl with 5 to 20 ring-forming atoms,         halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or         perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or         perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated         heteroaryl with 5 to 20 ring-forming atoms; or         -   at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵ are             bridged and form a 5 to 20 member ring;     -   m=0, 1, 2, 3 or 4;     -   M=a metal selected from the group comprising alkali metal,         alkaline earth metal, Al, Ga, In, transition metal or rare earth         metal;     -   L=charge neutral ligand which coordinates to the metal M,         selected from the group comprising H₂O, C₂ to C₄₀ mono- or         multi-dentate ethers and C₂ to C₄₀ thioethers, C₂ to C₄₀ amines,         C₂ to C₄₀ phosphine, C₂ to C₂₀ alkyl nitrile or C₂ to C₄₀ aryl         nitrile, or a compound according to Formula (III);

-   -   -   wherein R⁶ and R⁷ are independently selected from C₁ to C₂₀             alkyl, C₁ to C₂₀ heteroalkyl, C₆ to C₂₀ aryl, heteroaryl             with 5 to 20 ring-forming atoms, halogenated or             perhalogenated C₁ to C₂₀ alkyl, halogenated or             perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or             perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated             heteroaryl with 5 to 20 ring-forming atoms, or at least one             R⁶ and R⁷ are bridged and form a 5 to 20 member ring, or the             two R⁶ and/or the two R⁷ are bridged and form a 5 to 40             member ring or form a 5 to 40 member ring comprising an             unsubstituted or C₁ to C₁₂ substituted phenanthroline;

    -   p=0, 1, 2 or 3;

    -   A¹, A², A³ and A⁴ are independently selected from CO, SO₂ or         POR⁸;         -   R⁸=electron withdrawing group selected from the group             comprising halide, nitrile, halogenated or perhalogenated C₁             to C₂₀ alkyl, halogenated or perhalogenated C₆ to C₂₀ aryl,             or halogenated or perhalogenated heteroaryl with 5 to 20             ring-forming atoms;

    -   n=1, 2, 3, 4 or 5;

    -   B¹, B², B³ and B⁴ are same or independently selected from         substituted or unsubstituted C₁ to C₂₀ alkyl, substituted or         unsubstituted C₁ to C₂₀ heteroalkyl, substituted or         unsubstituted C₆ to C₂₀ aryl, substituted or unsubstituted C₅ to         C₂₀ heteroaryl, or B¹ and B² are bridged;

    -   wherein B¹ and B² are bridged, then:         -   M, N, A¹, B¹, B², A² and N form a 7 to 10 member ring             according to Formula Ib;

-   -   -    or         -   N, A¹, B¹, B² and A² form a 5 to 10 member ring according to             Formula Ic,

-   -   -    or         -   N, A¹, B¹, B² and A² form a first 5 to 10 member ring and B¹             and B² form a second 5 to 20 member ring according to             Formula Id:

According to another aspect of the present invention, there is provided a hole injection layer (HIL) for an OLED, wherein the hole injection layer comprises one triarylamine compound.

According to another aspect of the present invention, there is provided a hole injection layer (HIL) for an OLED, wherein the hole injection layer comprises one charge neutral metal amide compound.

According to another aspect of the present invention, there is provided a hole injection layer (HIL) for an OLED, wherein the hole injection layer comprises one triarylamine compound and one charge neutral metal amide compound.

According to another aspect of the present invention, there is provided a hole injection layer (HIL) for an OLED comprising a triarylamine compound with a HOMO more negative than −5 eV and more positive than −6 eV, when measured by cyclic voltammetry in dichloromethane vs. Fc/Fc⁺, preferably more negative than −5.05 eV and more positive than −5.9 eV. Under these conditions the HOMO of spiro-MeO-TAD (CAS 207739-72-8) is −4.71 eV.

According to another aspect of the present invention, there is provided a hole injection layer (HIL) for an OLED comprising a triarylamine compound with an oxidation potential more positive than—0.2 V and more negative than 1.22 V, when measured by cyclic voltammetry in dichloromethane vs. Fc/Fc⁺, preferably more positive than—0.18 V and more negative than 1.12 V. Under these conditions the oxidation potential of spiro-MeO-TAD (CAS 207739-72-8) is −0.07 V.

According to another aspect of the present invention, there is provided a hole injection layer (HIL) for an OLED comprising a triarylamine compound doped with a charge neutral metal amide compound, wherein the hole injection layer has a thickness of at least about ≥20 nm to about ≤1000 nm and the charge neutral metal amide compound has the Formula Ia:

-   -   wherein:     -   G=halide, O, alkoxylate or amine of Formula IIa to IIe:

-   -   R¹ to R⁵ are independently selected from the group comprising H,         C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to         C₁₂ substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂         substituted heteroaryl with 5 to 20 ring-forming atoms,         halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or         perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or         perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated         heteroaryl with 5 to 20 ring-forming atoms; or         -   at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵ are             bridged and form a 5 to 20 member ring;     -   m=0, 1, 2, 3 or 4;     -   M=a metal selected from the group comprising alkali metal,         alkaline earth metal, Al, Ga, In, transition metal or rare earth         metal;     -   L=charge neutral ligand which coordinates to the metal M,         selected from the group comprising H₂O, C₂ to C₄₀ mono- or         multi-dentate ethers and C₂ to C₄₀ thioethers, C₂ to C₄₀ amines,         C₂ to C₄₀ phosphine, C₂ to C₂₀ alkyl nitrile or C₂ to C₄₀ aryl         nitrile, or a compound according to Formula (III);

-   -   -   wherein R⁶ and R⁷ are independently selected from C₁ to C₂₀             alkyl, C₁ to C₂₀ heteroalkyl, C₆ to C₂₀ aryl, heteroaryl             with 5 to 20 ring-forming atoms, halogenated or             perhalogenated C₁ to C₂₀ alkyl, halogenated or             perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or             perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated             heteroaryl with 5 to 20 ring-forming atoms, or at least one             R⁶ and R⁷ are bridged and form a 5 to 20 member ring, or the             two R⁶ and/or the two R⁷ are bridged and form a 5 to 40             member ring or form a 5 to 40 member ring comprising an             unsubstituted or C₁ to C₁₂ substituted phenanthroline;

    -   p=0, 1, 2 or 3;

    -   A¹, A², A³ and A⁴ are independently selected from CO, SO₂ or         POR⁸;         -   R⁸=electron withdrawing group selected from the group             comprising halide, nitrile, halogenated or perhalogenated C₁             to C₂₀ alkyl, halogenated or perhalogenated C₆ to C₂₀ aryl,             or halogenated or perhalogenated heteroaryl with 5 to 20             ring-forming atoms;

    -   n=1, 2, 3, 4 or 5;

    -   B³ and B⁴ are same or independently selected from substituted or         unsubstituted C₁ to C₂₀ alkyl, substituted or unsubstituted C₁         to C₂₀ heteroalkyl, substituted or unsubstituted C₆ to C₂₀ aryl,         substituted or unsubstituted C₅ to C₂₀ heteroaryl;

    -   B¹ and B² are bridged, wherein:         -   M, N, A¹, B¹, B², A² and N form a 7 to 10 member ring             according to Formula Ib;

-   -   -    or         -   N, A¹, B¹, B² and A² form a 5 to 10 member ring according to             Formula Ic,

-   -   -    or         -   N, A¹, B¹, B² and A² form a first 5 to 10 member ring and B¹             and B² form a second 5 to 20 member ring according to             Formula Id:

According to another aspect of the present invention, there is provided a hole injection layer (HIL) comprising a triarylamine compound doped with a charge neutral metal amide compound, wherein the hole injection layer has a thickness of at least about ≥20 nm to about ≤1000 nm;

-   -   wherein the triarylamine compound has the Formula VIIa:

wherein:

-   -   Ar¹ and Ar²=independently selected from substituted or         unsubstituted C₆ to C₂₀ arylene;     -   Ar³ and Ar⁴=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl;     -   Ar⁵ and Ar⁶=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl or C₅ to C₄₀ heteroaryl;     -   R⁹=a single chemical bond, a unsubstituted or substituted C₁ to         C₆ alkyl and unsubstituted or substituted C₁ to C₅ heteroalkyl;     -   q=0, 1 or 2;     -   r=0 or 1;

wherein

-   -   the substituents for Ar¹ to Ar⁶ are independently selected from         C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, or halide; and     -   the substitutents for R⁹ are independently selected from C₁ to         C₆ alkyl, C₁ to C₅ heteroalkyl, C₆ to C₂₀ aryl and C₅ to C₂₀         heteroaryl;

wherein the charge neutral metal amide compound has the Formula Ia:

-   -   wherein:     -   G=halide, O, alkoxylate or amine of Formula IIa to IIe:

-   -   R¹ to R⁵ are independently selected from the group comprising H,         C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to         C₁₂ substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂         substituted heteroaryl with 5 to 20 ring-forming atoms,         halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or         perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or         perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated         heteroaryl with 5 to 20 ring-forming atoms; or         -   at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵ are             bridged and form a 5 to 20 member ring;     -   m=0, 1, 2, 3 or 4;     -   M=a metal selected from the group comprising alkali metal,         alkaline earth metal, Al, Ga, In, transition metal or rare earth         metal;         -   wherein the bond between N and the metal M is a covalent             bond or N forms a non-covalent interaction to the metal M;     -   L=charge neutral ligand which coordinates to the metal M,         selected from the group comprising H₂O, C₂ to C₄₀ mono- or         multi-dentate ethers and C₂ to C₄₀ thioethers, C₂ to C₄₀ amines,         C₂ to C₄₀ phosphine, C₂ to C₂₀ alkyl nitrile or C₂ to C₄₀ aryl         nitrile, or a compound according to Formula (III);

-   -   -   wherein R⁶ and R⁷ are independently selected from C₁ to C₂₀             alkyl, C₁ to C₂₀ heteroalkyl, C₆ to C₂₀ aryl, heteroaryl             with 5 to 20 ring-forming atoms, halogenated or             perhalogenated C₁ to C₂₀ alkyl, halogenated or             perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or             perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated             heteroaryl with 5 to 20 ring-forming atoms, or at least one             R⁶ and R⁷ are bridged and form a 5 to 20 member ring, or the             two R⁶ and/or the two R⁷ are bridged and form a 5 to 40             member ring or form a 5 to 40 member ring comprising an             unsubstituted or C₁ to C₁₂ substituted phenanthroline;

    -   p=0, 1, 2 or 3;

    -   A¹, A², A³ and A⁴ are independently selected from CO, SO₂ or         POR⁸;         -   R⁸=electron withdrawing group selected from the group             comprising halide, nitrile, halogenated or perhalogenated C₁             to C₂₀ alkyl, halogenated or perhalogenated C₆ to C₂₀ aryl,             or halogenated or perhalogenated heteroaryl with 5 to 20             ring-forming atoms;

    -   n=1, 2, 3, 4 or 5;

    -   B¹, B², B³ and B⁴ are same or independently selected from         substituted or unsubstituted C₁ to C₂₀ alkyl, substituted or         unsubstituted C₁ to C₂₀ heteroalkyl, substituted or         unsubstituted C₆ to C₂₀ aryl, substituted or unsubstituted C₅ to         C₂₀ heteroaryl, or B¹ and B² are bridged;

    -   wherein B¹ and B² are bridged, then:         -   M, N, A¹, B¹, B², A² and N form a 7 to 10 member ring             according to Formula Ib;

-   -   -    or         -   N, A¹, B¹, B² and A² form a 5 to 10 member ring according to             Formula Ic,

-   -   -    or         -   N, A¹, B¹, B² and A² form a first 5 to 10 member ring and B¹             and B² form a second 5 to 20 member ring according to             Formula Id:

According to another aspect of the present invention, there is provided a hole injection layer (HIL) comprising a triarylamine compound doped with a charge neutral metal amide compound, wherein the hole injection layer has a thickness of at least about ≥20 nm to about ≤1000 nm;

-   -   wherein the triarylamine compound has the Formula VIIa

wherein:

-   -   Ar¹ and Ar²=independently selected from substituted or         unsubstituted C₆ to C₂₀ arylene;     -   Ar³ and Ar⁴=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl;     -   Ar⁵ and Ar⁶=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl or C₅ to C₄₀ heteroaryl;     -   R⁹=a single chemical bond, a unsubstituted or substituted C₁ to         C₆ alkyl and unsubstituted or substituted C₁ to C₅ heteroalkyl;     -   q=0, 1 or 2;     -   r=0 or 1;     -   wherein         -   the substituents for Ar¹ to Ar⁶ are independently selected             from C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, or halide; and         -   the substitutents for R⁹ are independently selected from C₁             to C₆ alkyl, C₁ to C₅ heteroalkyl, C₆ to C₂₀ aryl and C₅ to             C₂₀ heteroaryl;     -   wherein the charge neutral metal amide compound has the Formula         Ia:

-   -   wherein:     -   G=halide, O, alkoxylate or amine of Formula IIa to IIe:

-   -   R¹ to R⁵ are independently selected from the group comprising H,         C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to         C₁₂ substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂         substituted heteroaryl with 5 to 20 ring-forming atoms,         halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or         perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or         perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated         heteroaryl with 5 to 20 ring-forming atoms; or         -   at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵ are             bridged and form a 5 to 20 member ring;     -   m=0, 1, 2, 3 or 4;     -   M=a metal selected from the group comprising alkali metal,         alkaline earth metal, Al, Ga, In, transition metal or rare earth         metal;         -   wherein the bond between N and the metal M is a covalent             bond or N forms a non-covalent interaction to the metal M;     -   L=charge neutral ligand which coordinates to the metal M,         selected from the group comprising H₂O, C₂ to C₄₀ mono- or         multi-dentate ethers and C₂ to C₄₀ thioethers, C₂ to C₄₀ amines,         C₂ to C₄₀ phosphine, C₂ to C₂₀ alkyl nitrile or C₂ to C₄₀ aryl         nitrile, or a compound according to Formula (III);

-   -   -   wherein R⁶ and R⁷ are independently selected from C₁ to C₂₀             alkyl, C₁ to C₂₀ heteroalkyl, C₆ to C₂₀ aryl, heteroaryl             with 5 to 20 ring-forming atoms, halogenated or             perhalogenated C₁ to C₂₀ alkyl, halogenated or             perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or             perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated             heteroaryl with 5 to 20 ring-forming atoms, or at least one             R⁶ and R⁷ are bridged and form a 5 to 20 member ring, or the             two R⁶ and/or the two R⁷ are bridged and form a 5 to 40             member ring or form a 5 to 40 member ring comprising an             unsubstituted or C₁ to C₁₂ substituted phenanthroline;

    -   p=0, 1, 2 or 3;

    -   A¹, A², A³ and A⁴ are independently selected from CO, SO₂ or         POR⁸;         -   R⁸=electron withdrawing group selected from the group             comprising halide, nitrile, halogenated or perhalogenated C₁             to C₂₀ alkyl, halogenated or perhalogenated C₆ to C₂₀ aryl,             or halogenated or perhalogenated heteroaryl with 5 to 20             ring-forming atoms;

    -   n=1, 2, 3, 4 or 5;

    -   B¹, B², B³ and B⁴ are same or independently selected from         substituted or unsubstituted C₁ to C₂₀ alkyl, substituted or         unsubstituted C₁ to C₂₀ heteroalkyl, substituted or         unsubstituted C₆ to C₂₀ aryl, substituted or unsubstituted C₅ to         C₂₀ heteroaryl, or B¹ and B² are bridged;

    -   wherein B¹ and B² are bridged, then:         -   M, N, A¹, B¹, B², A² and N form a 7 to 10 member ring             according to Formula Ib;

-   -   -    or         -   N, A¹, B¹, B² and A² form a 5 to 10 member ring according to             Formula Ic,

-   -   -    or         -   N, A¹, B¹, B² and A² form a first 5 to 10 member ring and B¹             and B² form a second 5 to 20 member ring according to             Formula Id:

wherein in the hole injection layer (HIL) the wt.-% of the triarylamine compound according to Formula VIIa is higher than the wt.-% of the charge neutral metal amide compound according to Formula Ia; wherein the weight-% of the components are based on the total weight of the hole injection layer.

It has been surprisingly found that the thick hole injection layer (HIL) of a triarylamine compound doped with a metal amide improves performance of OLEDs compared to a thick hole injection layer (HIL) of CNHAT (Dipyrazino[2,3-f:2′,3′-h]quinoxaline-2,3,6,7,10,11-hexacarbonitrile (CAS 105598-27-4)). CNHAT is a standard hole injection layer. Surprisingly, a hole injection layer (HIL) of a triarylamine compound doped with a metal amide of at least 20 nm are required to achieve good voltage stability.

It has been found that the thickness of the triarylamine hole injection layer (HIL) doped with an metal amide can be selected very thick, for example up to 450 nm, without a dramatic increase in voltage.

It has been further found that the thick hole injection layer (HIL) of a triarylamine compound doped with a metal amide according to the invention may be beneficially used for large area lighting panels, where the ITO is not sufficiently conductive, for example a copper grid.

Additionally, the thick hole injection layer material according to the invention may provide an effective smoothing layer and thereby provides a pinhole-free basis for deposition of subsequent layers. Thereby, defect-free OLEDs can be obtained even if the substrate is non-uniform.

In particular, the invention may provide an uniform hole injection layer on top of an anode layer which comprises metal oxides, for example indium-tin oxide (ITO), or a metal grid.

Further, the thick hole injection layer (HIL) of a triarylamine compound doped with a metal amide inserted between the anode and the hole transport layer effectively promotes hole injection into the hole transport layer. For example, if the HOMO level of the hole transport layer is further away from vacuum level, the performance of metal amides is superior to CNHAT, in particular the voltage. Furthermore, effective hole injection even into very deep HOMO HTLs (HOMO further away from vacuum level) can be achieved. This cannot be achieved with prior art materials, such as CNHAT, which is typically used as a HIL material. Efficient hole injection into very deep HOMO levels enables the use of high efficiency emission layers, in particular phosphorescent blue and green emitters and emission which relies on TADF (thermally activated delayed fluorescence).

A very deep HOMO in the sense of the present invention is a HOMO which is more negative than −5 eV, preferably more negative than −5.2 eV when measured by cyclic voltammetry in dichloromethane vs. Fc/Fc⁺.

According to another aspect of the present invention, there is provided a hole injection layer (HIL) comprising a triarylamine compound doped with a charge neutral metal amide compound, wherein the hole injection layer has a thickness of at least about ≥20 nm to about ≤1000 nm;

-   -   wherein the triarylamine compound has the Formula VIIa:

wherein:

-   -   Ar¹ and Ar²=independently selected from substituted or         unsubstituted C₆ to C₂₀ arylene;     -   Ar³ and Ar⁴=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl;     -   Ar⁵ and Ar⁶=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl or C₅ to C₄₀ heteroaryl;     -   R⁹=a single chemical bond, a unsubstituted or substituted C₁ to         C₆ alkyl;     -   q=0, 1 or 2;     -   r=0 or 1;     -   wherein         -   the substituents for Ar¹ to Ar⁶ are independently selected             from C₁ to C₂₀ alkyl or halide; and         -   the substitutents for R⁹ are independently selected from C₁             to C₆ alkyl, C₆ to C₂₀ aryl and C₅ to C₂₀ heteroaryl;     -   wherein the charge neutral metal amide compound has the Formula         Ia:

-   -   wherein:     -   G=halide, O, alkoxylate or amine of Formula IIa to IIe:

-   -   R¹ to R⁵ are independently selected from the group comprising H,         C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to         C₁₂ substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂         substituted heteroaryl with 5 to 20 ring-forming atoms,         halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or         perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or         perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated         heteroaryl with 5 to 20 ring-forming atoms; or         -   at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵ are             bridged and form a 5 to 20 member ring;     -   m=0, 1, 2, 3 or 4;     -   M=a metal selected from the group comprising alkali metal,         alkaline earth metal, Al, Ga, In, transition metal or rare earth         metal;         -   wherein the bond between N and the metal M is a covalent             bond or N forms a non-covalent interaction to the metal M;     -   L=charge neutral ligand which coordinates to the metal M,         selected from the group comprising H₂O, C₂ to C₄₀ mono- or         multi-dentate ethers and C₂ to C₄₀ thioethers, C₂ to C₄₀ amines,         C₂ to C₄₀ phosphine, C₂ to C₂₀ alkyl nitrile or C₂ to C₄₀ aryl         nitrile, or a compound according to Formula (III);

-   -   -   wherein R⁶ and R⁷ are independently selected from C₁ to C₂₀             alkyl, C₁ to C₂₀ heteroalkyl, C₆ to C₂₀ aryl, heteroaryl             with 5 to 20 ring-forming atoms, halogenated or             perhalogenated C₁ to C₂₀ alkyl, halogenated or             perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or             perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated             heteroaryl with 5 to 20 ring-forming atoms, or         -   at least one R⁶ and R⁷ are bridged and form a 5 to 20 member             ring, or the two R⁶ and/or the two R⁷ are bridged and form a             5 to 40 member ring or form a 5 to 40 member ring comprising             an unsubstituted or C₁ to C₁₂ substituted phenanthroline;

    -   p=0, 1, 2 or 3;

    -   A¹, A², A³ and A⁴ are independently selected from CO, SO₂ or         POR⁸;         -   R⁸=electron withdrawing group selected from the group             comprising halide, nitrile, halogenated or perhalogenated C₁             to C₂₀ alkyl, halogenated or perhalogenated C₆ to C₂₀ aryl,             or halogenated or perhalogenated heteroaryl with 5 to 20             ring-forming atoms;

    -   n=1, 2, 3, 4 or 5;

    -   B¹, B², B³ and B⁴ are same or independently selected from         substituted or unsubstituted C₁ to C₂₀ alkyl, substituted or         unsubstituted C₁ to C₂₀ heteroalkyl, substituted or         unsubstituted C₆ to C₂₀ aryl, substituted or unsubstituted C₅ to         C₂₀ heteroaryl, or B¹ and B² are bridged;

    -   wherein B¹ and B² are bridged, then:         -   M, N, A¹, B¹, B², A² and N form a 7 to 10 member ring             according to Formula Ib;

-   -   -    or         -   N, A¹, B¹, B² and A² form a 5 to 10 member ring according to             Formula Ic,

-   -   -    or         -   N, A¹, B¹, B² and A² form a first 5 to 10 member ring and B¹             and B² form a second 5 to 20 member ring according to             Formula Id:

The organic light-emitting diode (OLED) can be a bottom emission OLED or a top emission OLED.

For the following defined terms, these definitions shall be applied, unless a different definition is given in the claims or elsewhere in this specification.

The bond between N and the metal M, as indicated for example in Formula 1a, 1b, 1c, and 1d, can be a covalent bond or N forms a non-covalent interaction to the metal M. Without being bond to a specific theory it is assumed by the inventors that this kind of compounds may form a covalent bond between N and M or N forms a non-covalent interaction to the metal M, as can be seen from the example below:

The dotted line and/or an arrow symbolizes a non-covalent interaction. A non-covalent interaction differs from a covalent bond in that it does not involve the sharing of electrons, but rather involves more dispersed variations of electromagnetic interactions between molecules or within a molecule. Non-covalent interactions can be generally classified into four categories, electrostatic, π-effects, van der Waals forces, and hydrophobic effects.

The voltage, also named U, is measured in Volt (V) at 10 milliAmpere per square centimeter (mA/cm²) in bottom emission devices and at 15 mA/cm² in top emission devices.

The voltage stability over time U(50 h)-U(0 h) is measured in Volt (V) at 15 mA/cm². To calculate the voltage stability over time, the voltage at the start of the stability test (U(0 h)) is subtracted from the voltage after 50 hours (h) (U(50 h)). The smaller the value U(50 h)-U(0 h) is the better is the voltage stability over time.

The external quantum efficiency, also named EQE, is measured in percent (%). The color space is described by coordinates CIE-x and CIE-y (International Commission on Illumination 1931). For blue emission the CIE-y is of particular importance. A smaller CIE-y denotes a deeper blue color.

The highest occupied molecular orbital, also named HOMO, and lowest unoccupied molecular orbital, also named LUMO, are measured in electron volt (eV).

The term “OLED” and “organic light-emitting diode” is simultaneously used and having the same meaning.

The term “transition metal” means and includes any element in the d-block of the periodic table, which includes groups 3 to 12 elements on the periodic table.

As used herein, “weight percent”, “wt.-%”, “percent by weight”, “% by weight”, and variations thereof refer to a composition, component, substance or agent as the weight of that composition, component, substance or agent of the respective electron transport layer divided by the total weight of the composition thereof and multiplied by 100. It is understood that the total weight percent amount of all components, substances or agents of the respective electron transport layer are selected such that it does not exceed 100 wt.-%.

As used herein, “volume percent”, “vol.-%”, “percent by volume”, “% by volume”, and variations thereof refer to an elemental metal, a composition, component, substance or agent as the volume of that elemental metal, component, substance or agent of the respective electron transport layer divided by the total volume of the respective electron transport layer thereof and multiplied by 100. It is understood that the total volume percent amount of all elemental metal, components, substances or agents of the respective electron transport layer are selected such that it does not exceed 100 vol.-%.

All numeric values are herein assumed to be modified by the term “about”, whether or not explicitly indicated. As used herein, the term “about” refers to variation in the numerical quantity that can occur. Whether or not, modified by the term “about”, the claims include equivalents to the quantities.

It should be noted that, as used in this specification and the appended claims, the singular forms “a”, “an”, and “the” include plural referents unless the content clearly dictates otherwise.

The term “free of”, “does not contain”, “does not comprise” does not exclude impurities. Impurities have no technical effect with respect to the object achieved by the present invention.

The term “alkyl” refers to straight-chain or branched alkyl groups.

The term “1 to 20 carbon atoms” as used herein refers to straight-chain or branched alkyl groups having 1 to 20 carbon atoms. The alkyl groups can be selected from the group comprising methyl, ethyl and the isomers of propyl, butyl or pentyl, such as isopropyl, isobutyl, tert.-butyl, sec.-butyl and/or isopentyl. The term “aryl” refers to aromatic groups for example phenyl or naphthyl.

Herein, when a first element is referred to as being formed or disposed “on” a second element, the first element can be disposed directly on the second element or one or more other elements may be disposed there between. When a first element is referred to as being formed or disposed “directly on” a second element, no other elements are disposed there between.

According to another aspect, there is provided a hole injection layer (HIL) comprising a triarylamine compound doped with a charge neutral metal amide compound, wherein the hole injection layer has a thickness of at least about ≥20 nm to about ≤1000 nm:

wherein the triarylamine compound has the Formula VIIa:

wherein:

-   -   Ar¹ and Ar²=independently selected from substituted or         unsubstituted C₆ to C₂₀ arylene;     -   Ar³ and Ar⁴=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl;     -   Ar⁵ and Ar⁶=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl or C₅ to C₄₀ heteroaryl;     -   R⁹=a single chemical bond, a unsubstituted or substituted C₁ to         C₆ alkyl and unsubstituted or substituted C₁ to C₅ heteroalkyl;     -   q=0, 1 or 2;     -   r=0 or 1;     -   wherein         -   the substituents for Ar¹ to Ar⁶ are independently selected             from C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, or halide; and         -   the substitutents for R⁹ are independently selected from C₁             to C₆ alkyl, C₁ to C₅ heteroalkyl, C₆ to C₂₀ aryl and C₅ to             C₂₀ heteroaryl;     -   wherein the charge neutral metal amide compound has the Formula         Ia:

wherein:

-   -   G=halide, O, alkoxylate or amine of Formula IIa to IIe:

-   -   R¹ to R⁵ are independently selected from the group comprising H,         C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to         C₁₂ substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂         substituted heteroaryl with 5 to 20 ring-forming atoms,         halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or         perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or         perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated         heteroaryl with 5 to 20 ring-forming atoms; or         -   at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵ are             bridged and form a 5 to 20 member ring;     -   m=0, 1, 2, 3 or 4;     -   M=a metal selected from the group comprising alkali metal,         alkaline earth metal, Al, Ga, In, transition metal or rare earth         metal;         -   wherein the bond between N and the metal M is a covalent             bond or N forms a non-covalent interaction to the metal M;     -   L=charge neutral ligand which coordinates to the metal M,         selected from the group comprising H₂O, C₂ to C₄₀ mono- or         multi-dentate ethers and C₂ to C₄₀ thioethers, C₂ to C₄₀ amines,         C₂ to C₄₀ phosphine, C₂ to C₂₀ alkyl nitrile or C₂ to C₄₀ aryl         nitrile, or a compound according to Formula (III);

-   -   -   wherein R⁶ and R⁷ are independently selected from C₁ to C₂₀             alkyl, C₁ to C₂₀ heteroalkyl, C₆ to C₂₀ aryl, heteroaryl             with 5 to 20 ring-forming atoms, halogenated or             perhalogenated C₁ to C₂₀ alkyl, halogenated or             perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or             perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated             heteroaryl with 5 to 20 ring-forming atoms, or at least one             R⁶ and R⁷ are bridged and form a 5 to 20 member ring, or the             two R⁶ and/or the two R⁷ are bridged and form a 5 to 40             member ring or form a 5 to 40 member ring comprising an             unsubstituted or C₁ to C₁₂ substituted phenanthroline;

    -   p=0, 1, 2 or 3;

    -   A¹, A², A³ and A⁴ are independently selected from CO, SO₂ or         POR⁸;         -   R⁸=electron withdrawing group selected from the group             comprising halide, nitrile, halogenated or perhalogenated C₁             to C₂₀ alkyl, halogenated or perhalogenated C₆ to C₂₀ aryl,             or halogenated or perhalogenated heteroaryl with 5 to 20             ring-forming atoms;

    -   n=1, 2, 3, 4 or 5;

    -   B¹, B², B³ and B⁴ are same or independently selected from         substituted or unsubstituted C₁ to C₂₀ alkyl, substituted or         unsubstituted C₁ to C₂₀ heteroalkyl, substituted or         unsubstituted C₆ to C₂₀ aryl, substituted or unsubstituted C₅ to         C₂₀ heteroaryl.

According to another aspect there is provided a hole injection layer for an OLED comprising a charge neutral metal amide compound, wherein the charge neutral metal amide compound has the Formula Ib, Ic or Id:

wherein: B¹ and B² are bridged; B³ and B⁴ are same or independently selected from substituted or unsubstituted C₁ to C₂₀ alkyl, substituted or unsubstituted C₁ to C₂₀ heteroalkyl, substituted or unsubstituted C₆ to C₂₀ aryl, substituted or unsubstituted C₅ to C₂₀ heteroaryl;

-   -   M, N, A¹, B¹, B², A² and N form a 7 to 10 member ring according         to Formula Ib;

-   -    or     -   N, A¹, B¹, B² and A² form a 5 to 10 member ring according to         Formula Ic,

-   -   or     -   N, A¹, B¹, B² and A² form a first 5 to 10 member ring and B¹ and         B² form a second 5 to 20 member ring according to Formula Id:

wherein:

-   -   G=halide, O, alkoxylate or amine of Formula IIa to IIe:

-   -   R¹ to R⁵ are independently selected from the group comprising H,         C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to         C₁₂ substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂         substituted heteroaryl with 5 to 20 ring-forming atoms,         halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or         perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or         perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated         heteroaryl with 5 to 20 ring-forming atoms; or         -   at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵ are             bridged and form a 5 to 20 member ring;     -   m=0, 1, 2, 3 or 4;     -   M=a metal selected from the group comprising alkali metal,         alkaline earth metal, Al, Ga, In, transition metal or rare earth         metal;         -   wherein the bond between N and the metal M is a covalent             bond or N forms a non-covalent interaction to the metal M;     -   L=charge neutral ligand which coordinates to the metal M,         selected from the group comprising H₂O, C₂ to C₄₀ mono- or         multi-dentate ethers and C₂ to C₄₀ thioethers, C₂ to C₄₀ amines,         C₂ to C₄₀ phosphine, C₂ to C₂₀ alkyl nitrile or C₂ to C₄₀ aryl         nitrile, or a compound according to Formula (III);

-   -   -   wherein R⁶ and R⁷ are independently selected from C₁ to C₂₀             alkyl, C₁ to C₂₀ heteroalkyl, C₆ to C₂₀ aryl, heteroaryl             with 5 to 20 ring-forming atoms, halogenated or             perhalogenated C₁ to C₂₀ alkyl, halogenated or             perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or             perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated             heteroaryl with 5 to 20 ring-forming atoms, or at least one             R⁶ and R⁷ are bridged and form a 5 to 20 member ring, or the             two R⁶ and/or the two R⁷ are bridged and form a 5 to 40             member ring or form a 5 to 40 member ring comprising an             unsubstituted or C₁ to C₁₂ substituted phenanthroline;

    -   p=0, 1, 2 or 3;

    -   A¹, A², A³ and A⁴ are independently selected from CO, SO₂ or         POR⁸;         -   R⁸=electron withdrawing group selected from the group             comprising halide, nitrile, halogenated or perhalogenated C₁             to C₂₀ alkyl, halogenated or perhalogenated C₆ to C₂₀ aryl,             or halogenated or perhalogenated heteroaryl with 5 to 20             ring-forming atoms;

    -   n=1, 2, 3, 4 or 5;         wherein the hole injection layer comprises:

    -   at least about ≥1 wt.-% to about ≤50 wt.-%, preferably about ≥1         wt.-% to about ≤25 wt.-%, and more preferred about ≥2 wt.-% to         about ≤15 wt.-%, of a charge neutral metal amide compound         according to Formula Ia, and

    -   at least about ≥50 wt.-% to about ≤99 wt.-%, preferably about         ≥75 wt.-% to about ≤99 wt.-%, and more preferred about ≥85 wt.-%         to about ≤98 wt.-%, of a triarylamine compound according to         Formula VIIa; wherein the weight-% of the components are based         on the total weight of the hole injection layer.

According to another aspect there is provided a hole injection layer (HIL) comprising a triarylamine compound doped with a charge neutral metal amide compound, wherein the hole injection layer has a thickness of at least about ≥20 nm to about ≤1000 nm:

wherein the triarylamine compound has the Formula VIIa:

wherein:

-   -   Ar¹ and Ar²=independently selected from substituted or         unsubstituted C₆ to C₂₀ arylene;     -   Ar³ and Ar⁴=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl;     -   Ar⁵ and Ar⁶=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl or C₅ to C₄₀ heteroaryl;     -   R⁹=a single chemical bond, a unsubstituted or substituted C₁ to         C₆ alkyl and unsubstituted or substituted C₁ to C₅ heteroalkyl;     -   q=0, 1 or 2;     -   r=0 or 1;     -   wherein         -   the substituents for Ar¹ to Ar⁶ are independently selected             from C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, or halide; and         -   the substitutents for R⁹ are independently selected from C₁             to C₆ alkyl, C₁ to C₅ heteroalkyl, C₆ to C₂₀ aryl and C₅ to             C₂₀ heteroaryl;

wherein the charge neutral metal amide compound has the Formula Ib:

wherein: B¹ and B² are bridged; and M, N, A¹, B¹, B², A² and N form a 7 to 10 member ring according to Formula Ib;

wherein:

-   -   G=halide, O, alkoxylate or amine of Formula IIa to IIe:

-   -   R¹ to R⁵ are independently selected from the group comprising H,         C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to         C₁₂ substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂         substituted heteroaryl with 5 to 20 ring-forming atoms,         halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or         perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or         perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated         heteroaryl with 5 to 20 ring-forming atoms; or         -   at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵ are             bridged and form a 5 to 20 member ring;     -   m=0, 1, 2, 3 or 4;     -   M=a metal selected from the group comprising alkali metal,         alkaline earth metal, Al, Ga, In, transition metal or rare earth         metal;         -   wherein the bond between N and the metal M is a covalent             bond or N forms a non-covalent interaction to the metal M;     -   L=charge neutral ligand which coordinates to the metal M,         selected from the group comprising H₂O, C₂ to C₄₀ mono- or         multi-dentate ethers and C₂ to C₄₀ thioethers, C₂ to C₄₀ amines,         C₂ to C₄₀ phosphine, C₂ to C₂₀ alkyl nitrile or C₂ to C₄₀ aryl         nitrile, or a compound according to Formula (III);

-   -   -   wherein R⁶ and R⁷ are independently selected from C₁ to C₂₀             alkyl, C₁ to C₂₀ heteroalkyl, C₆ to C₂₀ aryl, heteroaryl             with 5 to 20 ring-forming atoms, halogenated or             perhalogenated C₁ to C₂₀ alkyl, halogenated or             perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or             perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated             heteroaryl with 5 to 20 ring-forming atoms, or at least one             R⁶ and R⁷ are bridged and form a 5 to 20 member ring, or the             two R⁶ and/or the two R⁷ are bridged and form a 5 to 40             member ring or form a 5 to 40 member ring comprising an             unsubstituted or C₁ to C₁₂ substituted phenanthroline;

    -   p=0, 1, 2 or 3;

    -   A¹ and A² are independently selected from CO, SO₂ or POR⁸;         -   R⁸=electron withdrawing group selected from the group             comprising halide, nitrile, halogenated or perhalogenated C₁             to C₂₀ alkyl, halogenated or perhalogenated C₆ to C₂₀ aryl,             or halogenated or perhalogenated heteroaryl with 5 to 20             ring-forming atoms;

    -   n=1, 2, 3, 4 or 5.

According to another aspect there is provided a hole injection layer (HIL) comprising a triarylamine compound doped with a charge neutral metal amide compound, wherein the hole injection layer has a thickness of at least about ≥20 nm to about ≤1000 nm:

wherein the triarylamine compound has the Formula VIIa:

wherein:

-   -   Ar¹ and Ar²=independently selected from substituted or         unsubstituted C₆ to C₂₀ arylene;     -   Ar³ and Ar⁴=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl;     -   Ar⁵ and Ar⁶=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl or C₅ to C₄₀ heteroaryl;     -   R⁹=a single chemical bond, a unsubstituted or substituted C₁ to         C₆ alkyl and unsubstituted or substituted C₁ to C₅ heteroalkyl;     -   q=0, 1 or 2;     -   r=0 or 1;     -   wherein         -   the substituents for Ar¹ to Ar⁶ are independently selected             from C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, or halide; and         -   the substitutents for R⁹ are independently selected from C₁             to C₆ alkyl, C₁ to C₅ heteroalkyl, C₆ to C₂₀ aryl and C₅ to             C₂₀ heteroaryl;     -   wherein the charge neutral metal amide compound has the Formula         Ic:

wherein: B¹ and B² are bridged; and N, A¹, B¹, B² and A² form a 5 to 10 member ring according to Formula Ic,

wherein:

-   -   G=halide, O, alkoxylate or amine of Formula IIa to IIe:

-   -   R¹ to R⁵ are independently selected from the group comprising H,         C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to         C₁₂ substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂         substituted heteroaryl with 5 to 20 ring-forming atoms,         halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or         perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or         perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated         heteroaryl with 5 to 20 ring-forming atoms; or         -   at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵ are             bridged and form a 5 to 20 member ring;     -   m=0, 1, 2, 3 or 4;         -   M=a metal selected from the group comprising alkali metal,             alkaline earth metal, Al, Ga, In, transition metal or rare             earth metal;         -   wherein the bond between N and the metal M is a covalent             bond or N forms a non-covalent interaction to the metal M;     -   L=charge neutral ligand which coordinates to the metal M,         selected from the group comprising H₂O, C₂ to C₄₀ mono- or         multi-dentate ethers and C₂ to C₄₀ thioethers, C₂ to C₄₀ amines,         C₂ to C₄₀ phosphine, C₂ to C₂₀ alkyl nitrile or C₂ to C₄₀ aryl         nitrile, or a compound according to Formula (III);

-   -   -   wherein R⁶ and R⁷ are independently selected from C₁ to C₂₀             alkyl, C₁ to C₂₀ heteroalkyl, C₆ to C₂₀ aryl, heteroaryl             with 5 to 20 ring-forming atoms, halogenated or             perhalogenated C₁ to C₂₀ alkyl, halogenated or             perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or             perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated             heteroaryl with 5 to 20 ring-forming atoms, or at least one             R⁶ and R⁷ are bridged and form a 5 to 20 member ring, or the             two R⁶ and/or the two R⁷ are bridged and form a 5 to 40             member ring or form a 5 to 40 member ring comprising an             unsubstituted or C₁ to C₁₂ substituted phenanthroline;

    -   p=0, 1, 2 or 3;

    -   A¹ and A² are independently selected from CO, SO₂ or POR⁸;         -   R⁸=electron withdrawing group selected from the group             comprising halide, nitrile, halogenated or perhalogenated C₁             to C₂₀ alkyl, halogenated or perhalogenated C₆ to C₂₀ aryl,             or halogenated or perhalogenated heteroaryl with 5 to 20             ring-forming atoms;

    -   n=1, 2, 3, 4 or 5.

According to another aspect there is provided a hole injection layer (HIL) comprising a triarylamine compound doped with a charge neutral metal amide compound, wherein the hole injection layer has a thickness of at least about ≥20 nm to about ≤1000 nm:

wherein the triarylamine compound has the Formula VIIa:

-   -   wherein:     -   Ar¹ and Ar²=independently selected from substituted or         unsubstituted C₆ to C₂₀ arylene;     -   Ar³ and Ar⁴=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl;     -   Ar⁵ and Ar⁶=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl or C₅ to C₄₀ heteroaryl;     -   R⁹=a single chemical bond, a unsubstituted or substituted C₁ to         C₆ alkyl and unsubstituted or substituted C₁ to C₅ heteroalkyl;     -   q=0, 1 or 2;     -   r=0 or 1;     -   wherein         -   the substituents for Ar¹ to Ar⁶ are independently selected             from C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, or halide; and         -   the substitutents for R⁹ are independently selected from C₁             to C₆ alkyl, C₁ to C₅ heteroalkyl, C₆ to C₂₀ aryl and C₅ to             C₂₀ heteroaryl;     -   wherein the charge neutral metal amide compound has the Formula         Id:

wherein: B¹ and B² are bridged; and N, A¹, B¹, B² and A² form a first 5 to 10 member ring and B¹ and B² form a second 5 to 20 member ring according to Formula Id:

-   -   wherein:     -   G=halide, O, alkoxylate or amine of Formula IIa to IIe:

-   -   R¹ to R⁵ are independently selected from the group comprising H,         C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to         C₁₂ substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂         substituted heteroaryl with 5 to 20 ring-forming atoms,         halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or         perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or         perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated         heteroaryl with 5 to 20 ring-forming atoms; or         -   at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵ are             bridged and form a 5 to 20 member ring;     -   m=0, 1, 2, 3 or 4;     -   M=a metal selected from the group comprising alkali metal,         alkaline earth metal, Al, Ga, In, transition metal or rare earth         metal;         -   wherein the bond between N and the metal M is a covalent             bond or N forms a non-covalent interaction to the metal M;     -   L=charge neutral ligand which coordinates to the metal M,         selected from the group comprising H₂O, C₂ to C₄₀ mono- or         multi-dentate ethers and C₂ to C₄₀ thioethers, C₂ to C₄₀ amines,         C₂ to C₄₀ phosphine, C₂ to C₂₀ alkyl nitrile or C₂ to C₄₀ aryl         nitrile, or a compound according to Formula (III);

-   -   -   wherein R⁶ and R⁷ are independently selected from C₁ to C₂₀             alkyl, C₁ to C₂₀ heteroalkyl, C₆ to C₂₀ aryl, heteroaryl             with 5 to 20 ring-forming atoms, halogenated or             perhalogenated C₁ to C₂₀ alkyl, halogenated or             perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or             perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated             heteroaryl with 5 to 20 ring-forming atoms, or at least one             R⁶ and R⁷ are bridged and form a 5 to 20 member ring, or the             two R⁶ and/or the two R⁷ are bridged and form a 5 to 40             member ring or form a 5 to 40 member ring comprising an             unsubstituted or C₁ to C₁₂ substituted phenanthroline;

    -   p=0, 1, 2 or 3;

    -   A¹ and A² are independently selected from CO, SO₂ or POR⁸;         -   R⁸=electron withdrawing group selected from the group             comprising halide, nitrile, halogenated or perhalogenated C₁             to C₂₀ alkyl, halogenated or perhalogenated C₆ to C₂₀ aryl,             or halogenated or perhalogenated heteroaryl with 5 to 20             ring-forming atoms;

    -   n=1, 2, 3, 4 or 5.

According to another aspect there is provided a hole injection layer (HIL) comprising a triarylamine compound doped with a charge neutral metal amide compound, wherein the hole injection layer has a thickness of at least about ≥20 nm to about ≤1000 nm:

wherein the triarylamine compound has the Formula VIIa:

wherein:

-   -   Ar¹ and Ar²=independently selected from substituted or         unsubstituted C₆ to C₂₀ arylene;     -   Ar³ and Ar⁴=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl;     -   Ar⁵ and Ar⁶=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl or C₅ to C₄₀ heteroaryl;     -   R⁹=a single chemical bond, a unsubstituted or substituted C₁ to         C₆ alkyl and unsubstituted or substituted C₁ to C₅ heteroalkyl;     -   q=0, 1 or 2;     -   r=0 or 1;     -   wherein         -   the substituents for Ar¹ to Ar⁶ are independently selected             from C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, or halide; and         -   the substitutents for R⁹ are independently selected from C₁             to C₆ alkyl, C₁ to C₅ heteroalkyl, C₆ to C₂₀ aryl and C₅ to             C₂₀ heteroaryl;

wherein the charge neutral metal amide compound has the Formula Ib, Ic, or Id:

-   -   wherein:     -   G=halide, O, alkoxylate or amine of Formula IIa to IIe:

-   -   R¹ to R⁵ are independently selected from the group comprising H,         C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to         C₁₂ substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂         substituted heteroaryl with 5 to 20 ring-forming atoms,         halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or         perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or         perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated         heteroaryl with 5 to 20 ring-forming atoms; or         -   at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵ are             bridged and form a 5 to 20 member ring;     -   m=0, 1, 2, 3 or 4;     -   M=a metal selected from the group comprising alkali metal,         alkaline earth metal, Al, Ga, In, transition metal or rare earth         metal;         -   wherein the bond between N and the metal M is a covalent             bond or N forms a non-covalent interaction to the metal M;     -   L=charge neutral ligand which coordinates to the metal M,         selected from the group comprising H₂O, C₂ to C₄₀ mono- or         multi-dentate ethers and C₂ to C₄₀ thioethers, C₂ to C₄₀ amines,         C₂ to C₄₀ phosphine, C₂ to C₂₀ alkyl nitrile or C₂ to C₄₀ aryl         nitrile, or a compound according to Formula (III);

-   -   -   wherein R⁶ and R⁷ are independently selected from C₁ to C₂₀             alkyl, C₁ to C₂₀ heteroalkyl, C₆ to C₂₀ aryl, heteroaryl             with 5 to 20 ring-forming atoms, halogenated or             perhalogenated C₁ to C₂₀ alkyl, halogenated or             perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or             perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated             heteroaryl with 5 to 20 ring-forming atoms, or at least one             R⁶ and R⁷ are bridged and form a 5 to 20 member ring, or the             two R⁶ and/or the two R⁷ are bridged and form a 5 to 40             member ring or form a 5 to 40 member ring comprising an             unsubstituted or C₁ to C₁₂ substituted phenanthroline;

    -   p=0, 1, 2 or 3;

    -   A¹, A², A³ and A⁴ are independently selected from CO, SO₂ or         POR⁸;         -   R⁸=electron withdrawing group selected from the group             comprising halide, nitrile, halogenated or perhalogenated C₁             to C₂₀ alkyl, halogenated or perhalogenated C₆ to C₂₀ aryl,             or halogenated or perhalogenated heteroaryl with 5 to 20             ring-forming atoms;

    -   n=1, 2, 3, 4 or 5;

    -   B³ and B⁴ are same or independently selected from substituted or         unsubstituted C₁ to C₂₀ alkyl, substituted or unsubstituted C₁         to C₂₀ heteroalkyl, substituted or unsubstituted C₆ to C₂₀ aryl,         substituted or unsubstituted C₅ to C₂₀ heteroaryl;

    -   B¹ and B² are bridged,

    -   wherein:         -   M, N, A¹, B¹, B², A² and N form a 7 to 10 member ring             according to Formula Ib;

-   -   -    or         -   N, A¹, B¹, B² and A² form a 5 to 10 member ring according to             Formula Ic,

-   -   -    or         -   N, A¹, B¹, B² and A² form a first 5 to 10 member ring and B¹             and B² form a second 5 to 20 member ring according to             Formula Id:

According to another aspect for the charge neutral metal amide compound according to the invention B¹, B², B³ and B⁴ can be independently selected from a substituted C₁ to C₂₀ alkyl, substituted C₁ to C₂₀ heteroalkyl, substituted C₆ to C₂₀ aryl, or substituted C₅ to C₂₀ heteroaryl; wherein the substituent of the substituted C₁ to C₂₀ alkyl, substituted C₁ to C₂₀ heteroalkyl, substituted C₆ to C₂₀ aryl, or substituted C₅ to C₂₀ heteroaryl;

-   -   wherein the substituent can be an electron withdrawing group         selected from the group comprising a halide, nitrile,         perhalogenated C₁ to C₂₀ alkyl, perhalogenated C₆ to C₂₀ aryl,         perhalogenated heteroaryl with 6 to 20 ring-forming atoms,         preferably the electron withdrawing group is a fluoride,         perfluroinated C₁ to C₂₀ alkyl, perfluorinated C₆ to C₂₀ aryl,         or perfluorinated heteroaryl with 5 to 20 ring-forming atoms.

In order to increase the vacuum vaporization it can be preferred that according to one embodiment for the charge neutral metal amide compound the substituent can be a C₁ to C₆ alkyl or C₁ to C₆ heteroalkyl, and more preferred an C₁ to C₄ alkyl or C₁ to C₄ heteroalkyl.

In order to improve the solution processing it can be preferred that according to one embodiment for the charge neutral metal amide compound the substituent can be a C₄ to C₂₀ alkyl or C₄ to C₂₀ heteroalkyl, and more preferred an C₆ to C₁₈ alkyl or C₆ to C₁₈ heteroalkyl.

According to one aspect the charge neutral ligand L may be selected from the group comprising C₂ to C₂₀ glycole ethers, C₂ to C₂₀ ethylendiamine derivatives, and more preferred bis(2-methoxyethyl) ether, tetrahydrofurane, tetrahydrothiophen, N¹,N¹,N²,N²-tetramethyl-1, 2-ethanediamine, N-((E,2E)-2-{[(E)-1,1-dimethylethyl]imino}ethylidene)-2-methyl-2-propanamine, acetonitrile, trisphenylphosphine, trismethylphosphine, tris(cylcohexyl)phosphine, 1,2-bis(diphenylphosphino)ethane, bispyridine, phenanthroline, (2E,3E)-N²,N³-diphenylbutane-2,3-diimine or (1E,2E)-N¹,N²,1,2-tetraphenylethane-1,2-diimine.

According to one aspect of the charge neutral metal amide compound “m” may be selected that m=0, 1 or 2.

According to one aspect of the charge neutral metal amide compound “M” may be selected from Li(I), Na(I), K(I), Cs(I), Mg(II), Ca(II), Sr(II), Ba(II), Sc(III), Y(III), Ti(IV), V(III-V), Cr(III-VI), Mn(II), Mn(III), Fe(II), Fe(III), Co(II), Co(III), Ni(II), Cu(I), Cu(II), Zn(II), Ag(I), Au(I), Au(III), Al(III), Ga(III), In(III), Sn(II), Sn(IV), or Pb(II); preferably M is selected from Li (I), Mg (II), Mn (II) or Ag (I); and more preferred M is selected from Mg (II) and Li (I).

According to one aspect of the charge neutral metal amide compound, wherein may be (G)_(m) for m=1, then G is Cl; or may be (G)_(m) for m=2, then G is O.

According to one aspect of the charge neutral metal amide compound, wherein may be (G)_(m)-M is Cl—Al, Cl—Mg, O═V or O₂U.

According to one aspect of the charge neutral metal amide compound, wherein may be for n≥2 then:

-   -   N, A¹, B¹, A² and B² form a 5 to 10 member ring; or     -   M, N, A¹, B¹, A² and B² form a 7 to 10 member ring; or     -   M, N, A¹, B¹, A² and B² form a 7 to 10 member ring and A³, B³,         A⁴ and B⁴ form a 5 to 10 member ring.

According to another aspect the charge neutral ligand L may the Formula Ia,

wherein:

-   -   A¹ and A² are same or independently selected from CO, POR⁸ and         SO₂, preferably A¹ and A² are selected same from CO, POR⁸, SO₂;         or     -   A¹ and A² are independently selected from CO, POR⁸, SO₂, and     -   N, A¹, B¹, A² and B² form a 5 to 10 member ring.

According to another aspect the charge neutral metal amide compound of the hole injection layer may be selected from at least one compound according to Formula IIa, Hb, Hc, IId, IIe, IIf; IIg and/or IIh,

wherein for:

-   -   p=0, m=1, 2, 3 or 4 and n=1, 2, 3 or 4, the charge neutral metal         amide compound has the Formula Ha:

-   -    or     -   p=1, 2 or 3, and n=1, 2, 3 or 4 and m=0, the charge neutral         metal amide compound has the Formula Hb:

-   -    or     -   p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, A¹, B¹, B²         and A² form a 5 to 10 member ring, the charge neutral metal         amide compound has the Formula He:

-   -    or     -   p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, A¹, B¹, B²         and A² form a first 5 to 10 member ring and B¹ and B² are         bridged to form a second 5 to 20 member ring, the charge neutral         metal amide compound has the Formula Hd:

-   -    or     -   p=1, 2 or 3, n=1, m=1, 2, 3 or 4, and M, N, A¹, B¹, B², A² and N         form a 7 to 10 member ring, the charge neutral metal amide         compound has the Formula IIe:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, A¹, B¹, B² and A² form a         5 to 10 member ring, the charge neutral metal amide compound has         the Formula IIf:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, A¹, B¹, B² and A² form a         first 5 to 10 member ring, and B¹ and B² are bridged to form a         second 5 to 20 member ring, the charge neutral metal amide         compound has the Formula IIg:

-   -   p=1, 2 or 3, n=1, m=0 and M, N, A¹, B¹, B², A² and N form a 7 to         10 member ring, the charge neutral metal amide compound has the         Formula IIh:

According to another aspect the charge neutral metal amide compound of the hole injection layer may be selected from at least one compound according to Formula IIIa, IIIb, IIIc, IIId, IIIe, IIIf, IIIg, IIIh and/or IIIi,

wherein for A¹ and A² are SO₂:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4, the charge neutral         metal amide compound has the Formula IIIa:

-   -   p=0, n=1, 2, 3 or 4, m=1, 2, 3 or 4, the charge neutral metal         amide compound has the Formula IIIb:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=0, the charge neutral metal amide         compound has the Formula IIIc:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, SO₂, B¹, B²         and SO₂ form a 5 to 10 member ring, the charge neutral metal         amide compound has the Formula IIId:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, SO₂, B¹, B²         and SO₂ form a first 5 to 10 member ring, and B¹ and B² are         bridged to form a second 5 to 20 member ring, the charge neutral         metal amide compound has the Formula IIIe:

-   -   p=1, 2 or 3, n=1, m=1, 2, 3 or 4 and M, N, SO₂, B¹, B², SO₂ and         N form a 7 to 10 member ring, the charge neutral metal amide         compound has the Formula IIIf:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, SO₂, B¹, B² and SO₂ form         a 5 to 10 member ring, the charge neutral metal amide compound         has the Formula IIIg:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, SO₂, B¹, B² and SO₂ form         a first 5 to 10 member ring, and B¹ and B² are bridged to form a         second 5 to 20 member ring, the charge neutral metal amide         compound has the Formula IIIh:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and M, N, SO₂, B¹, B², SO₂ and         N form a 7 to 10 member ring, the charge neutral metal amide         compound has the Formula IIIi:

According to another aspect the charge neutral metal amide compound of the hole injection layer may be selected from at least one compound according to Formula IVa, IVb, IVc, IVd and/or IVe,

wherein for A¹ and A² are POR⁸:

-   -   p=1, 2 or 3, m=1, 2, 3 or 4 and n=1, 2, 3 or 4, the charge         neutral metal amide compound has the Formula IVa:

-   -   p=0, m=1, 2, 3 or 4 and n=1, 2, 3 or 4, the charge neutral metal         amide compound has the Formula IVb:

-   -   p=1, 2 or 3, m=0 and n=1, 2, 3 or 4, the charge neutral metal         amide compound has the Formula IVc:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, POR⁸, B¹, B²         and POR⁸ form a 5 to 10 member ring, the charge neutral metal         amide compound has the Formula (IVd):

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, POR⁸, B¹, B² and POR⁸         form a 5 to 10 member ring, the charge neutral metal amide         compound has the Formula (IVe):

According to another aspect the charge neutral metal amide compound of the hole injection layer may be selected from at least one compound according to Formula Va, Vb, Vc, Vd, Ve, Vf, Vg, Vh and/or Vi,

wherein for A¹ and A² are CO:

-   -   p=1, 2 or 3, m=1, 2, 3 or 4 and n=1, 2, 3 or 4, the charge         neutral metal amide compound has the Formula Va:

-   -   p=0, n=1, 2, 3 or 4, m=1, 2, 3 or 4, the charge neutral metal         amide compound has the Formula Vb:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=0, the charge neutral metal amide         compound has the Formula Vc:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, CO, B¹, B²         and CO form a 5 to 10 member ring, the charge neutral metal         amide compound has the Formula Vd:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, CO, B¹, B²         and CO form a first 5 to 10 member ring, and B¹ and B² are         bridged to form a second 5 to 20 member ring, the charge neutral         metal amide compound has the Formula Ve:

-   -   p=1, 2 or 3, n=1, m=1, 2, 3 or 4 and M, N, CO, B¹, B², CO and N         form a 7 to 10 member ring, the charge neutral metal amide         compound has the Formula Vf:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, CO, B¹, B² and CO form a         5 to 10 member ring, the charge neutral metal amide compound has         the Formula (Vg):

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, CO, B¹, B² and CO form a         first 5 to 10 member ring, and B¹ and B² form a second 5 to 20         member ring, the charge neutral metal amide compound has the         Formula Vh:

-   -   p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and M, N, CO, B¹, B², CO and N         form a 7 to 10 member ring, the charge neutral metal amide         compound has the Formula (Vi):

According to another aspect the charge neutral metal amide compound of the hole injection layer may be selected from at least one compound according to Formula VIa, wherein for A¹ is SO₂ and A² is POR⁸:

-   -   p=1, 2 or 3, m=1, 2, 3 or 4 and n=1, 2, 3 or 4, the charge         neutral metal amide compound has the Formula VIa:

According to another aspect the charge neutral metal amide compound of the hole injection layer may be selected from at least one compound according to Formula Ib:

wherein:

-   -   A³ and A⁴ are same or independently selected from CO, POR⁸ or         SO₂, preferably A³ and A⁴ are selected same from CO, POR⁸ or         SO₂;     -   B³ and B⁴ are independently selected from substituted or         unsubstituted C₁ to C₂₀ alkyl, substituted or unsubstituted C₁         to C₂₀ heteroalkyl, substituted or unsubstituted C₆ to C₂₀ aryl,         substituted or unsubstituted C₆ to C₂₀ heteroaryl, preferably B³         and B⁴ are selected same; and     -   M, N, A¹, B¹, A² and B² form a 7 to 10 member ring.

According to another aspect the charge neutral metal amide compound of the hole injection layer may be selected from at least one compound according to Formula Id, wherein N, A¹, B¹, A² and B² form a first 5 to 10 member ring and B¹ and B² are bridged to form a second ring of a substituted or unsubstituted C₆ to C₂₀ aryl, or of a substituted or unsubstituted C₆ to C₂₀ heteroaryl ring:

According to another aspect the charge neutral metal amide compound of the hole injection layer may be selected from at least one fluorinated compound according to:

-   -   Formula C1 to C16, based on general formula Ia, wherein p=0,         m=0, n=1, 2, 3 or 4 and A¹ and A² are SO₂:

-   -   Formula C17 to C23, based on general Formula Ia, wherein n=1, 2,         3 or 4, A¹ and A² are CO:

-   -   Formula C24 to C25, based on general Formula Ia, wherein n=1, 2,         3 or 4, A¹ and A² are POR⁸:

According to another aspect the charge neutral metal amide compound of the hole injection layer may be selected from at least one fluorinated compound, based on general formula Ia, having the Formula D1 to D24:

wherein p=0, m=0, n=1, 2, 3 or 4 and A¹ and A² are SO₂:

According to another aspect the charge neutral metal amide compound of the hole injection layer may be selected from at least one fluorinated compound, based on general formula Ia, having the Formula F1 to F23:

wherein the charge neutral ligand L coordinates to the metal M:

wherein

-   R⁶ and R⁷ are independently selected from C₁ to C₂₀ alkyl, C₁ to C₂₀     heteroalkyl, C₆ to C₂₀ aryl, heteroaryl with 5 to 20 ring-forming     atoms, halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or     perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or perhalogenated     C₆ to C₂₀ aryl, halogenated or perhalogenated heteroaryl with 5 to     20 ring-forming atoms, or at least one R⁶ and R⁷ are bridged and     form a 5 to 20 member ring, or the two R⁶ and/or the two R⁷ are     bridged and form a 5 to 40 member ring or form a 5 to 40 member ring     comprising an unsubstituted or C₁ to C₁₂ substituted phenanthroline.

Charge neutral metal amide compounds which contain a charge-neutral ligand L selected from mono and multidental ethers or amines forming a 5 to 7 membered ring system with the metal, preferably glycole ethers, ethylendiamine derivatives, even more preferred diglyme, and/or N1,N1,N2,N2-tetramethyl-1,2-ethanediamine, N-((E,2E)-2-{[(E)-1,1-dimethylethyl]imino}ethylidene)-2-methyl-2-propanamine can be preferably used as HIL-material.

Examples of charge neutral metal amides compounds with a charge-neutral ligand L selected from mono and/or multidental ethers or amines that can be preferably used as HIL-material having the Formula F1, F2, F3, F4, F5 and/or F6:

-   wherein -   R⁶ and R⁷ are independently selected from C₁ to C₂₀ alkyl, C₁ to C₂₀     heteroalkyl, C₆ to C₂₀ aryl, heteroaryl with 5 to 20 ring-forming     atoms, halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or     perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or perhalogenated     C₆ to C₂₀ aryl, halogenated or perhalogenated heteroaryl with 5 to     20 ring-forming atoms, or at least one R⁶ and R⁷ are bridged and     form a 5 to 20 member ring, or the two R⁶ and/or the two R⁷ are     bridged and form a 5 to 40 member ring or form a 5 to 40 member ring     comprising an unsubstituted or C₁ to C₁₂ substituted phenanthroline.

According to another aspect the charge neutral metal amide compound of the hole injection layer may be selected preferably from at least one fluorinated compound, based on general formula Ia, having the Formula F18 to F23:

According to another aspect the charge neutral metal amide compound of the hole injection layer may be selected preferably from at least one fluorinated compound, based on general formula Ia, having the Formula F24 to F45:

wherein a halide, O, alkoxylate or amine bonds to the metal M:

wherein

-   R¹ to R⁵ are independently selected from the group comprising H, C₁     to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to C₁₂     substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂ substituted     heteroaryl with 5 to 20 ring-forming atoms, halogenated or     perhalogenated C₁ to C₂₀ alkyl, halogenated or perhalogenated C₁ to     C₂₀ heteroalkyl, halogenated or perhalogenated C₆ to C₂₀ aryl,     halogenated or perhalogenated heteroaryl with 5 to 20 ring-forming     atoms; or at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵     are bridged and form a 5 to 20 member cyclic ring.

More preferred are compounds which comprise a ligand G. Ligand G is selected from group VII elements, preferably chloride Cl. Furthermore preferred are compounds wherein ligand G is selected from an alkoxylate of formula F30, F31 and F35:

-   wherein -   R¹ is selected from the group comprising H, C₁ to C₂₀ alkyl, C₁ to     C₂₀ heteroalkyl, unsubstituted or C₁ to C₁₂ substituted C₆ to C₂₀     aryl, unsubstituted or C₁ to C₁₂ substituted heteroaryl with 5 to 20     ring-forming atoms, halogenated or perhalogenated C₁ to C₂₀ alkyl,     halogenated or perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or     perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated     heteroaryl with 5 to 20 ring-forming atoms.

According to another aspect the charge neutral metal amide compound of the hole injection layer may be selected preferably from at least one fluorinated compound, based on general formula Ia, having the Formula F36 to F46:

In Table 1 below metal amide compounds according to formula Ia are listed, which can be preferably used as hole injection layer (HIL) material.

TABLE 1 Compounds of formula (Ia) which can be suitable used for an hole injection layer (HIL) Metal amide Structure CAS number Li TFSI

90076-65-6 Na TFSI

91742-21-1 K TFSI

90076-67-8 Cs TFSI

91742-16-4 Mg (TFSI)₂

133395-16-1 Fe (TFSI)₃

207861-59-4 Ag TFSI

189114-61-2 Mn (TFSI)₂

207861-55-0 Sn (TFSI)₄

1019840-51-7 Sm (TFSI)₃

222733-67-7 Lu (TFSI)₃

887919-24-6 Sc (TFSI)₃

176726-07-1 Nd (TFSI)₃

207861-67-4 U(O)₂ (TFSI)₂

943217-83-2 V(O) (TFSI)₃

—

Particularly preferred are metal amide compounds for use as HIL-material listed in Table 2.

TABLE 2 Compounds of formula (Ia) which can be suitable used for an hole injection layer (HIL)

According to one aspect, the hole injection layer (HIL) may comprises the charge neutral metal amide compound according to formula Ia, Ib, Ic and/or Id in the range of about ≥0.1 wt.-% to about ≤49 wt.-%, preferably about ≥0.5 wt.-% to about ≤45 wt.-%, further preferred about ≥1 wt.-% to about ≤40 wt.-%, in addition preferred about ≥1.5 wt.-% to about ≤30 wt.-%, or about ≥2 wt.-% to about ≤20 wt.-%, or about ≥2.5 wt.-% to about ≤10 wt.-%, or about ≥3 wt.-% to about ≤7 wt.-%, and more preferred about ≥3.5 wt.-% to about ≤5 wt.-% or about ≥4 wt.-% to about ≤4.5 wt.-%.

Triarylamine Compounds Used in the Hole Transport Layer (HIL)

According to a preferred aspect, the hole injection layer (HIL) comprises a triarylamine compound having the Formula VIIa:

wherein:

-   -   Ar¹ and Ar²=independently selected from substituted or         unsubstituted C₆ to C₂₀ arylene;     -   Ar³ and Ar⁴=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl;     -   Ar⁵ and Ar⁶=independently selected from substituted or         unsubstituted C₆ to C₂₀ aryl or C₅ to C₄₀ heteroaryl;     -   R⁹=a single chemical bond, a unsubstituted or substituted C₁ to         C₆ alkyl and unsubstituted or substituted C₁ to C₅ heteroalkyl;     -   q=0, 1 or 2;     -   r=0 or 1;         wherein     -   the substituents for Ar¹ to Ar⁶ are independently selected from         C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, or halide; and     -   the substitutents for R⁹ are independently selected from C₁ to         C₆ alkyl, C₁ to C₅ heteroalkyl, C₆ to C₂₀ aryl and C₅ to C₂₀         heteroaryl.

According to a further preferred aspect, the hole injection layer may comprises a triarylamine compound of Formula VIIa, wherein Ar¹ and Ar² are Ph; Ar³ to Ar⁶ are selected from phenyl, tolyl, xylyl, mesityl, biphenyl, 1-naphthyl, 2-napthyl, 2-(9,9-dialkyl-fluorenyl), 2-(9-alkyl-9′-aryl-fluorenyl) and 2-(9,9-diaryl-fluorenyl); R⁹=single bond; r=1 and q=1.

According to a further preferred aspect, the hole injection layer may comprises a triarylamine compound of Formula VIIa, wherein Ar¹ and Ar² are independently selected from phenyl and biphenyl; Ar³ to Ar⁶ are selected from phenyl, tolyl, xylyl, mesityl, biphenyl, 1-naphthyl, 2-napthyl, 2-(9,9-dialkyl-fluorenyl), 2-(9-alkyl-9′-aryl-fluorenyl) and 2-(9,9-diaryl-fluorenyl); R⁹=single bond; r=1 and q=1.

According to a further preferred aspect, the hole injection layer may comprises a triarylamine compound of Formula VIIa, wherein Ar¹ and Ar² are phenyl; Ar³ to Ar⁶ are selected from phenyl, tolyl, xylyl, mesityl, biphenyl, 1-naphthyl, 2-napthyl, 2-(9,9-dialkyl-fluorenyl), 2-(9-alkyl-9′-aryl-fluorenyl) and 2-(9,9-diaryl-fluorenyl); R⁹=9,9′-fluorenyl; r=1 and q=1.

According to a further preferred aspect, the hole injection layer may comprises a triarylamine compound of Formula VIIa, wherein Ar¹ is phenyl; Ar³ to Ar⁶ are selected from phenyl, tolyl, xylyl, mesityl, biphenyl, 1-naphthyl, 2-napthyl, 2-(9,9-dialkyl-fluorenyl), 2-(9-alkyl-9′-aryl-fluorenyl) and 2-(9,9-diaryl-fluorenyl); R⁹=single bond; r=0 and q=1. The substituent on Ar¹ is selected from phenyl, biphenyl, 2-(9,9-dialkyl-fluorenyl), 2-(9-alkyl-9′-aryl-fluorenyl) and 2-(9,9-diaryl-fluorenyl).

According to a further preferred aspect, the hole injection layer may comprises a triarylamine compound of Formula VIIa, wherein N, Ar¹ and Ar³ form a carbazole ring; Ar² is phenyl or biphenyl; Ar³ to Ar⁶ are selected from phenyl, tolyl, xylyl, mesityl, biphenyl, 1-naphthyl, 2-napthyl, 2-(9,9-dialkyl-fluorenyl), 2-(9-alkyl-9′-aryl-fluorenyl) and 2-(9,9-diaryl-fluorenyl); R⁹=single bond; r=1 and q=1.

Preferably in Formula VIIa the q may be selected from 1 or 2.

Compounds of formula VIIa that can be suitable used as HIL-material may have an molecular weight suitable for thermal vacuum deposition and HOMO levels that provides a good hole injection performance into the emission layer. Compounds of formula VIIa that can be preferably used as HIL-material may have an molecular weight that is about ≥243 g/mol and about ≤2000 g/mol, even more preferred is about ≥412 g/mol and about ≤1800 g/mol, also preferred about ≥488 g/mol and about ≤1500 g/mol.

According to a more preferred embodiment the Ar¹ and Ar² of Formula VIIa may be independently selected from phenylene, biphenylene, naphthylene, anthranylene, carbazolylene, or fluorenylene, preferably from phenylene or biphenylene.

According to a more preferred embodiment the Ar³ to Ar⁶ of Formula VIIa may be independently selected from phenyl, biphenyl, terphenyl, quartphenyl, fluorenyl, napthyl, anthranyl, phenanthryl, thiophenyl, fluorenyl, or carbazolyl.

Even more preferred, Ar³ to Ar⁶ of Formula VIIa may be independently selected from phenyl, biphenyl, fluorenyl, napthyl, thiopheneyl, fluorenyl, or carbazolyl.

At least two of Ar¹ to Ar⁶ of Formula VIIa may form a cyclic structure, for example Ar¹ and Ar³; or Ar¹ and Ar⁴; or Ar² and Ar^(y); or Ar² and Ar⁶; may be a carbazole, phenazoline or phenoxazine ring.

According to a further preferred embodiment the triarylamine compound having the Formula VIIa, wherein:

-   -   Ar¹ and Ar² are independently selected from phenylene,         biphenylene, naphthylene, anthranylene, carbazolylene and         fluorenylene, preferably selected from phenylene and         biphenylene;     -   Ar³ to Ar⁶ are independently selected from phenyl, biphenyl,         terphenyl, quartphenyl, fluorenyl, napthyl, anthranyl,         phenanthryl, thiophenyl, fluorenyl, 9-carbazolyl; preferably     -   Ar³ to Ar⁶ are independently selected from phenyl, biphenyl,         fluorenyl, napthyl, thiophenyl, fluorenyl, carbazolyl.

Furthermore preferred, at least one of Ar¹ to Ar⁶ of Formula VIIa may be unsubstituted, even more preferred at least two of Ar¹ to Ar⁶ of Formula VII may be unsubstituted.

According to an additional preferred embodiment the triarylamine compound having the Formula VIIa:

-   -   Ar³ and Ar⁴ and/or Ar⁵ and Ar⁶ are linked to form a carbazole,         phenazoline or phenoxazine ring.

According to a furthermore preferred embodiment the triarylamine compound has the Formula VIIb to VIIk.

Compounds of formula VIIa, wherein not all Ar¹ to Ar⁶ are substituted are particularly suited for vacuum thermal deposition.

Preferably, the hole injection layer (HIL) may comprises a triarylamine compound of formula VIIa, wherein the substituents on Ar³ to Ar⁶ are independently selected from C₁ to C₁₂ alkyl, C₁ to C₁₂ alkoxy or halide, preferably from C₁ to C₈ alkyl or C₁ to C₈ heteroalkyl, even more preferred from C₁ to C₅ alkyl or C₁ to C₅ heteroalkyl.

Preferably, the hole injection layer comprises a triarylamine compound of formula VIIa, wherein the substituents on Ar³ to Ar⁶ are independently selected from C₁ to C₁₂ alkyl or halide, preferably from C₁ to C₈ alkyl or fluoride, even more preferred from C₁ to C₅ alkyl or fluoride. When the substituents are selected from alkyl groups, the HOMO level of the hole injection layer may have a HOMO level suitable for good hole injection into the emission layer, in particular of phosphorescent blue and green emitters and emission which relies on TADF (thermally activated delayed fluorescence) and the OLED may have low voltage, high efficiency and good stability.

Examples of particularly preferred compounds of Formula VIIa are shown in Table 3.

TABLE 3 Triarylamine compounds of formula VIIa HOMO Name Structure (eV) N,N,N′,N′-Tetrakis(4- methylphenyl)- benzidine (T-1)

−4.99 N4,N4,N4′,N4′- tetra(biphenyl-4- yl)biphenyl-4,4′- diamine (T-2)

−5.08 Biphenyl-4-yl(9,9- diphenyl-9H-fluoren- 2-yl)-[4-(9- phenyl-9H-carbazol- 3-yl)phenyl]-amine (T-3)

−5.10 N,N′-Bis(naphthalen- 1-yl)-N,N′- bis(phenyl)-benzidine (T-4)

−5.11 N1,N3-di([1,1′- biphenyl]-4-yl)-5- (9,9-dimethyl-9H- fluoren-2- yl)-N1,N3-bis(3,5- dimethylphenyl) benzene-1,3- diamine (T-5)

−5.18 N1,N3-di([1,1′- biphenyl]-4-yl)-5-(9,9- dimethyl-9H-fluoren- 2-yl)-N1,N3- dimesitylbenzene-1,3- diamine (T-6)

−5.22 N,N′-((9H-fluorene- 9,9-diyl)bis(4,1- phenylene))bis(N- ([1,1′-biphenyl]-4- yl)-[1,1′-biphenyl]- 4-amine) (T-7)

−5.24 N,N4″-di(naphthalen- 1-yl)-N4,N4″- diphenyl-[1,1′:4′,1″- terphenyl]- 4,4″-diamine (CAS 139255-16-6) (T-8)

−5.25 4,4′-Bis-(N-(1- naphthyl)- N-phenyl-amino)- quarterphenyl (CAS 650609-47-5) (T-9)

−5.33 4,4′,4″-Tris(carbazol- 9-yl)-triphenylamine (T-10)

−5.7 

According to another aspect, the hole injection layer (HIL) may have a layer thickness of at least about ≥30 nm to about ≤1000 nm, preferably of about ≥40 nm to about ≤500 nm, also preferred of about ≥50 nm to about ≤750 nm.

According to another aspect, the hole injection layer (HIL) may have a layer thickness of at least about ≥40 nm to about ≤1000 nm, preferably of about ≥60 nm to about ≤500 nm, also preferred of about ≥80 nm to about ≤750 nm.

According to another aspect, the hole injection layer (HIL) may have a layer thickness of at least about ≥70 nm to about ≤1000 nm, preferably of about ≥90 nm to about ≤500 nm, also preferred of about ≥100 nm to about ≤600 nm.

According to another aspect, the hole injection layer (HIL) may have a layer thickness of at least about ≥100 nm to about ≤1000 nm, preferably of about ≥150 nm to about ≤500 nm, also preferred of about ≥200 nm to about ≤450 nm.

According to another aspect, the hole injection layer (HIL) may comprises:

-   -   at least about ≥0.1 wt.-% to about ≤50 wt.-%, preferably about         ≥1 wt.-% to about ≤25 wt.-%, and more preferred about ≥2 wt.-%         to about ≤15 wt.-%, of a charge neutral metal amide compound         according to Formula Ia, Ib, Ic or Id, and     -   at least about ≥50 wt.-% to about ≤99 wt.-%, preferably about         ≥75 wt.-% to about ≤99 wt.-%, and more preferred about ≥85 wt.-%         to about ≤98 wt.-%, of a triarylamine compound; preferably the         wt.-% of the triarylamine compound is higher than the wt.-% of         the charge neutral metal amide compound; wherein the weight-% of         the components are based on the total weight of the hole         injection layer.

According to another aspect, the hole injection layer (HIL) may comprises:

-   -   at least about ≥0.5 wt.-% to about ≤50 wt.-%, preferably about         ≥1 wt.-% to about ≤25 wt.-%, and more preferred about ≥1.5 wt.-%         to about ≤15 wt.-%, of a charge neutral metal amide compound         according to Formula Ia, Ib, Ic or Id, and     -   at least about ≥50 wt.-% to about ≤99.5 wt.-%, preferably about         ≥75 wt.-% to about ≤99 wt.-%, and more preferred about ≥85 wt.-%         to about ≤98.5 wt.-%, of a triarylamine compound; wherein the         weight-% of the components are based on the total weight of the         hole injection layer.

According to another aspect, the hole injection layer (HIL) may comprises:

-   -   at least about ≥0.1 wt.-% to about ≤50 wt.-%, preferably about         ≥1 wt.-% to about ≤25 wt.-%, and more preferred about ≥2 wt.-%         to about ≤15 wt.-%, of a charge neutral metal amide compound         according to Formula Ia, Ib, Ic or Id, and     -   at least about ≥50 wt.-% to about ≤99 wt.-%, preferably about         ≥75 wt.-% to about ≤99 wt.-%, and more preferred about ≥85 wt.-%         to about ≤98 wt.-%, of a triarylamine compound according to         Formula VIIa; preferably the wt.-% of the triarylamine compound         is higher than the wt.-% of the charge neutral metal amide         compound; wherein the weight-% of the components are based on         the total weight of the hole injection layer.

According to another aspect, the hole injection layer (HIL) may comprises:

-   -   at least about ≥0.5 wt.-% to about ≤50 wt.-%, preferably about         ≥1 wt.-% to about ≤25 wt.-%, and more preferred about ≥1.5 wt.-%         to about ≤15 wt.-%, of a charge neutral metal amide compound         according to Formula Ia, Ib, Ic or Id, and     -   at least about ≥50 wt.-% to about ≤99.5 wt.-%, preferably about         ≥75 wt.-% to about ≤99 wt.-%, and more preferred about ≥85 wt.-%         to about ≤98.5 wt.-%, of a triarylamine compound according to         Formula VIIa; wherein the weight-% of the components are based         on the total weight of the hole injection layer.

According to another aspect, the hole injection layer (HIL) may comprises the triarylamine compound according to Formula VIIa in the range of about ≥60 wt.-% to about ≤100 wt.-%, further preferred about ≥70 wt.-% to about ≤100 wt.-%, in addition preferred about ≥80 wt.-% to about ≤100 wt.-%, or about ≥95 wt.-% to about ≤100 wt.-%, or about ≥98 wt.-% to about ≤100 wt.-%, or about ≥99 wt.-% to about ≤100 wt.-%, and more preferred about ≥90 wt.-% to about ≤100 wt.-% or about ≥95 wt.-% to about ≤99 wt.-%.

According to another aspect, the hole injection layer (HIL) may comprises the triarylamine compound according to Formula VIIa in the range of about ≥70 wt.-% to about ≤100 wt.-%, in addition preferred about ≥80 wt.-% to about ≤100 wt.-%, or about ≥95 wt.-% to about ≤100 wt.-%, or about ≥98 wt.-% to about ≤100 wt.-%, or about ≥99 wt.-% to about ≤100 wt.-%, and more preferred about ≥90 wt.-% to about ≤100 wt.-% or about ≥95 wt.-% to about ≤99 wt.-%.

According to another aspect, the hole injection layer (HIL) may comprises the triarylamine compound according to Formula VIIa in the range of about ≥80 wt.-% to about ≤100 wt.-%, or about ≥95 wt.-% to about ≤100 wt.-%, or about ≥98 wt.-% to about ≤100 wt.-%, or about ≥99 wt.-% to about ≤100 wt.-%, and more preferred about ≥90 wt.-% to about ≤100 wt.-% or about ≥95 wt.-% to about ≤99 wt.-%.

According to another aspect, the hole injection layer (HIL) may comprises the triarylamine compound according to Formula VIIa in the range of about ≥95 wt.-% to about ≤100 wt.-%, or about ≥98 wt.-% to about ≤100 wt.-%, or about ≥99 wt.-% to about ≤100 wt.-%, and more preferred about ≥90 wt.-% to about ≤100 wt.-% or about ≥95 wt.-% to about ≤99 wt.-%.

According to another aspect, the hole injection layer (HIL) may comprises the triarylamine compound according to Formula VIIa in the range of about ≥98 wt.-% to about ≤100 wt.-%, or about ≥99 wt.-% to about ≤100 wt.-%, and more preferred about ≥90 wt.-% to about ≤100 wt.-% or about ≥95 wt.-% to about ≤99 wt.-%.

According to another aspect, the hole injection layer (HIL) may comprises the triarylamine compound according to Formula VIIa in the range of about ≥99 wt.-% to about ≤100 wt.-%, and more preferred about ≥90 wt.-% to about ≤100 wt.-% or about ≥95 wt.-% to about ≤99 wt.-%.

According to another aspect, the hole injection layer comprises:

-   -   at least about ≥1 wt.-% to about ≤50 wt.-%, preferably about ≥1         wt.-% to about ≤25 wt.-%, and more preferred about ≥2 wt.-% to         about ≤15 wt.-%, of a charge neutral metal amide compound         according to claims 1 to 18, and     -   at least about ≥50 wt.-% to about ≤99 wt.-%, preferably about         ≥75 wt.-% to about ≤99 wt.-%, and more preferred about ≥85 wt.-%         to about ≤98 wt.-%, of a triarylamine compound; preferably the         wt.-% of the triarylamine compound is higher than the wt.-% of         the charge neutral metal amide compound; wherein the weight-% of         the components are based on the total weight of the hole         injection layer; or     -   at least about ≥1 wt.-% to about ≤4 wt.-%, and more preferred         about ≥2 wt.-% to about ≤3 wt.-%, of the charge neutral metal         amide compound; and     -   at least about ≤99 wt.-% to about ≥96 wt.-%, and more preferred         about ≤98 wt.-% to about ≥97 wt.-%, of the triarylamine         compound; preferably the wt.-% of the triarylamine compound is         higher than the wt.-% of the charge neutral metal amide         compound; wherein         the weight-% of the components are based on the total weight of         the hole injection layer.

Compounds Used in the Hole Transport Layer (HTL)

The HTL may be formed of any compound that is commonly used to form a HTL. Compound that can be suitably used is disclosed for example in Y. Shirota and H. Kageyama, Chem. Rev. 2007, 107, 953-1010 and incorporated by reference. Examples of the compound that may be used to form the HTL 140 are: a carbazole derivative, such as N-phenylcarbazole or polyvinylcarbazole; an amine derivative having an aromatic condensation ring, such as N,N′-bis(3-methylphenyl)-N,N′-diphenyl-[1,1-biphenyl]-4,4′-diamine (T-1), or N,N′-di(naphthalene-1-yl)-N,N′-diphenyl benzydine (alpha NPD, T-4); and a triphenylamine-based compound, such as 4,4′,4″-tris(N-carbazolyl)triphenylamine (T-10). Among these compounds, T-10 can transport holes and inhibit excitons from being diffused into the EML.

Other examples of the compounds that may be used forming the HTL 140 are oligothiophenes and phthalocyanines disclosed for example in Yasuhiko Shirota and Hiroshi Kageyama, Chem. Rev. 2007, 107, 953-1010 and in Facchetti, MaterialsToday 10, 2007, 28 and incorporated by reference.

Compounds Used in the Electron Transport Layer (ETL)

The OLED according to the present invention may not contain an electron transport layer (ETL). However, the OLED according to the present invention may optional contain an electron transport layer (ETL).

According to various embodiments the OLED may comprises an electron transport layer or an electron transport layer stack comprising at least a first electron transport layer and at least a second electron transport layer.

According to various embodiments of the OLED of the present invention the electron transport layer may comprises at least one matrix compound.

According to various embodiments of the OLED the matrix compound may be selected from:

-   -   an anthracene based compound or a heteroaryl substituted         anthracene based compound, preferably         2-(4-(9,10-di(naphthalen-2-yl)anthracene-2-yl)phenyl)-1-phenyl-1H-benzo[d]imidazole         and/or         N4,N4″-di(naphthalen-1-yl)-N4,N4″-diphenyl-[1,1′:4′,1″-terphenyl]-4,4″-diamine;     -   a phosphine oxide based compound, preferably         (3-(dibenzo[c,h]acridin-7-yl)phenyl)diphenylphosphine oxide         and/or phenyl bis(3-(pyren-1-yl)phenyl)phosphine oxide and/or         3-Phenyl-3H-benzo[b]dinaphtho[2,1-d:1′,2′-f]phosphepine-3-oxide;         or     -   a substituted phenanthroline compound, preferably         2,4,7,9-tetraphenyl-1,10-phenanthroline,         4,7-diphenyl-2,9-di-p-tolyl-1,10-phenanthroline, or         2,9-di(biphenyl-4-yl)-4,7-diphenyl-1,10-phenanthroline.

According to various embodiments of the OLED the matrix compound of the electron transport layer may be preferably selected from:

-   -   a phosphine oxide based compound, preferably         (3-(dibenzo[c,h]acridin-7-yl)phenyl)diphenylphosphine oxide,         3-phenyl-3H-benzo[b]dinaphtho[2,1-d:1′,2′-f]phosphepine-3-oxide         and/or phenyl bis(3-(pyren-1-yl)phenyl)phosphine oxide; or     -   a substituted phenanthroline compound, preferably         2,4,7,9-tetraphenyl-1,10-phenanthroline,         4,7-diphenyl-2,9-di-p-tolyl-1,10-phenanthroline, or         2,9-di(biphenyl-4-yl)-4,7-diphenyl-1,10-phenanthroline.

According to various embodiments of the OLED the matrix compound of the electron transport layer may be more preferred selected from:

-   -   a phosphine oxide based compound, preferably         (3-(dibenzo[c,h]acridin-7-yl)phenyl)diphenylphosphine oxide,         3-phenyl-3H-benzo[b]dinaphtho[2,1-d:1′,2′-f]phosphepine-3-oxide         and/or phenyl bis(3-(pyren-1-yl)phenyl)phosphine oxide.

According to various embodiments of the OLED of the present invention the thicknesses of the electron transport layer may be in the range of about ≥0.5 nm to about ≤95 nm, preferably of about ≥3 nm to about ≤80 nm, further preferred of about ≥5 nm to about ≤60 nm, also preferred of about ≥6 nm to about ≤40 nm, in addition preferred about ≥8 nm to about ≤20 nm and more preferred of about ≥10 nm to about ≤18 nm.

According to various embodiments of the OLED of the present invention the thicknesses of the electron transport layer stack can be in the range of about ≥25 nm to about ≤100 nm, preferably of about ≥30 nm to about ≤80 nm, further preferred of about ≥35 nm to about ≤60 nm, and more preferred of about ≥36 nm to about ≤40 nm.

According to various embodiments of the OLED of the present invention the electron transport layer may comprises:

-   -   a) about ≥10 wt.-% to about ≤70 wt.-%, preferably about ≥20         wt.-% to about ≤65 wt.-% and also preferred about ≥50 wt.-% to         about ≤60 wt.-% of a lithium halide or an lithium organic         complex of a lithium quinolate, a lithium borate, a lithium         phenolate and/or a lithium Schiff base, preferably of a lithium         quinolate complex has the formula I, II or III:

-   -   wherein         -   A1 to A6 are same or independently selected from CH, CR, N,             O,         -   R is same or independently selected from hydrogen, halogen,             alkyl or aryl or heteroaryl with 1 to 20 carbon atoms, and             more preferred of a lithium 8-hydroxyquinolate;     -   b) about ≤90 wt.-% to about ≥30 wt.-%, preferably about ≤80         wt.-% to about ≥35 wt.-% and also preferred about ≤50 wt.-% to         about ≥40 wt.-% of a matrix compound of:         -   an anthracene based compound or a hetero substituted             anthracene based compound, preferably             2-(4-(9,10-di(naphthalen-2-yl)anthracene-2-yl)phenyl)-1-phenyl-1H-benzo[d]imidazole             and/or             N4,N4″-di(naphthalen-1-yl)-N4,N4″-diphenyl-[1,1′:4′,1″-terphenyl]-4,4″-diamine;             or         -   a phosphine oxide based compound, preferably             (3-(dibenzo[c,h]acridin-7-yl)phenyl)diphenylphosphine oxide             and/or phenyl bis(3-(pyren-1-yl)phenyl)phosphine oxide             and/or             3-Phenyl-3H-benzo[b]dinaphtho[2,1-d:1′,2′-f]phosphepine-3-oxide;             or         -   a substituted phenanthroline compound, preferably             2,4,7,9-tetraphenyl-1,10-phenanthroline,             4,7-diphenyl-2,9-di-p-tolyl-1,10-phenanthroline, or             2,9-di(biphenyl-4-yl)-4,7-diphenyl-1,10-phenanthroline;             whereby     -   more preferred is a phosphine oxide based compound and most         preferred is         (3-(dibenzo[c,h]acridin-7-yl)phenyl)diphenylphosphine oxide;         based on the total weight of the electron transport layer.

According to one embodiment of the OLED, the electron transport layer comprises of about ≥50 wt.-% to about ≤60 wt.-% of a first lithium halide or a first lithium organic complex and about ≤50 wt.-% to about ≥40 wt.-% of a matrix compound of:

-   -   a phosphine oxide based compound, preferably         (3-(dibenzo[c,h]acridin-7-yl)phenyl)diphenylphosphine oxide,         3-phenyl-3H-benzo[b]dinaphtho[2,1-d:1′,2′-f]phosphepine-3-oxide         and/or phenyl bis(3-(pyren-1-yl)phenyl)phosphine oxide; or     -   a substituted phenanthroline compound, preferably         2,4,7,9-tetraphenyl-1,10-phenanthroline,         4,7-diphenyl-2,9-di-p-tolyl-1,10-phenanthroline, or         2,9-di(biphenyl-4-yl)-4,7-diphenyl-1,10-phenanthroline.

The light-emitting diode (OLED) may comprises at least two electrodes, an anode electrode and a second cathode electrode.

The electron transport layer/s or electron transport layer stack is not an electrode. The electron transport layer/s or electron transport layer are sandwiched between two electrodes, namely sandwiched between an anode and a second cathode.

The ETL may be formed optional on an EML or on the HBL if the HBL is formed. The ETL includes a first layer including a first lithium halide or a first lithium organic complex; and optional a second electron transport layer including a second lithium halide or a second lithium organic complex, wherein optional the first lithium organic complex is not the same as the second lithium organic complex and wherein the first lithium halide is not the same as the second lithium halide.

The ETL includes a first layer comprising a first matrix compound and a lithium halide or a lithium organic complex; and optional a second electron transport layer comprising a second matrix compound and a metal dopant selected from a group comprising alkali, alkaline earth and rare earth metals.

The ETL includes a first layer comprising a first matrix compound and a lithium halide or a lithium organic complex; and optional a second electron transport layer comprising a second matrix compound and is free of dopant.

The ETL may have a stacked structure, preferably of two ETL-layers, so that injection and transport of electrons may be balanced and holes may be efficiently blocked. In a conventional OLED, since the amounts of electrons and holes vary with time, after driving is initiated, the number of excitons generated in an emission area may be reduced. As a result, a carrier balance may not be maintained, so as to reduce the lifetime of the OLED.

However, in the ETL, the first layer and the second layer may have similar or identical energy levels, so that the carrier balance may be uniformly maintained, while controlling the electron-transfer rate.

Matrix compound for the electron layer that can be suitable used are selected from the group comprising anthracene compounds, preferably 2-(4-(9,10-di(naphthalen-2-yl)anthracen-2-yl)phenyl)-1-phenyl-1H-benzo[d]imidazole

Anthracene compounds that can be used as matrix materials are disclosed in U.S. Pat. No. 6,878,469 B.

Other matrix compounds that can be used are diphenylphosphine oxide, preferably (3-(dibenzo[c,h]acridin-7-yl)phenyl)diphenylphosphine oxide, phenylbis(3-(pyren-1-yl)phenyl)phosphine oxide, 3-phenyl-3H-benzo[b]dinaphtho[2,1-d:1′,2′-f]phosphepine-3-oxide, phenyldi(pyren-1-yl)phosphine oxide.

Diphenylphosphine oxide compounds that can be used as matrix materials are disclosed in EP 2395571 A1, WO2013079217 A1, EP 13187905, EP13199361 and JP2002063989 A1.

Other suitable matrix compounds that can be used are phenanthroline compounds, preferably selected from the group comprising of 2,4,7,9-tetraphenyl-1,10-phenanthroline, 4,7-diphenyl-2,9-di-p-tolyl-1,10-phenanthroline, and 2,9-di(biphenyl-4-yl)-4,7-diphenyl-1,10-phenanthroline. Phenanthroline compounds that can be used as matrix materials are disclosed in EP 1786050 A1.

The matrix compound of the electron transport layer may be a compound that efficiently transports electrons, such as an anthracene-based compound, diphenylphosphine oxide based compound, or a phenanthroline based compound, preferably a matrix compound mentioned in Table 4. For example, the matrix compound of the electron transport layer may be selected from the group consisting of Compound 5, a compound represented by Formula 2, and a compound represented by Formula 3 below:

In Formulae 2 and 3, R₁ to R₆ are each independently a hydrogen atom, a halogen atom, a hydroxy group, a cyano group, a substituted or unsubstituted C₁-C₃₀ alkyl group, a substituted or unsubstituted C₁-C₃₀ alkoxy group, a substituted or unsubstituted C₁-C₃₀ acyl group, a substituted or unsubstituted C₂-C₃₀ alkenyl group, a substituted or unsubstituted C₂-C₃₀ alkynyl group, a substituted or unsubstituted C₆-C₃₀ aryl group, or a substituted or unsubstituted C₃-C₃₀ heteroaryl group. At least two adjacent R₁ to R₆ groups are optionally bonded to each other, to form a saturated or unsaturated ring. L₁ is a bond, a substituted or unsubstituted C₁-C₃₀ alkylene group, a substituted or unsubstituted C₆-C₃₀ arylene group, or a substituted or unsubstituted C₃-C₃₀ hetero arylene group. Q₁ through Q₉ are each independently a hydrogen atom, a substituted or unsubstituted C₆-C₃₀ aryl group, or a substituted or unsubstituted C₃-C₃₀ hetero aryl group, and “a” is an integer from 1 to 10.

For example, R₁ to R₆ may be each independently selected from the group consisting of a hydrogen atom, a halogen atom, a hydroxy group, a cyano group, a methyl group, an ethyl group, a propyl group, a butyl group, a methoxy group, an ethoxy group, a propoxy group, a butoxy group, a phenyl group, a naphthyl group, an anthryl group, a pyridinyl group, and a pyrazinyl group.

In particular, in Formula 2 and/or 3, R₁ to R₄ may each be a hydrogen atom, R₅ may be selected from the group consisting of a halogen atom, a hydroxy group, a cyano group, a methyl group, an ethyl group, a propyl group, a butyl group, a methoxy group, an ethoxy group, a propoxy group, a butoxy group, a phenyl group, a naphthyl group, an anthryl group, a pyridinyl group, and a pyrazinyl group. In addition, in Formula 3, R₁ to R₆ may each be a hydrogen atom.

For example, in Formula 2 and/or 3, Q₁ to Q₉ are each independently a hydrogen atom, a phenyl group, a naphthyl group, an anthryl group, a pyridinyl group, and a pyrazinyl group. In particular, in Formulae 2 and/or 3, Q₁, Q₃-Q₆, Q₈ and Q₉ are hydrogen atoms, and Q₂ and Q₇ may be each independently selected from the group consisting of a phenyl group, a naphthyl group, an anthryl group, a pyridinyl group, and a pyrazinyl group.

For example, L₁, in Formula 2 and/or 3, may be selected from the group consisting of a phenylene group, a naphthylene group, an anthrylene group, a pyridinylene group, and a pyrazinylene group. In particular, L₁ may be a phenylene group or a pyridinylene group. For example, “a” may be 1, 2, or, 3.

The matrix compound for the ETL-layer may be further selected from Compound 5, 6, or 7 below:

TABLE 4 Chemical structures of matrix materials that can be suitable used for ETL-layer Referred to as: IUPAC name Structure Reference MX 1 2-(4-(9,10-di(naphthalen-2- yl)anthracen-2-yl)phenyl)-1- phenyl-1H- benzo[d]imidazole

US 6878469 B2. MX 2 (3-(dibenzo[c,h]acridin-7- yl)phenyl)diphenylphosphine oxide

EP 2395571B1, WO2013079217A1 MX 3 Phenylbis(3-(pyren-1- yl)phenyl)phosphine oxide

EP13187905.8 MX 4 3-Phenyl-3H- benzo[b]dinaphtho[2,1- d:1′,2′-f]phosphepine-3- oxide

EP13199361.0 MX 5 Phenyldi(pyren-1- yl)phosphine oxide

JP4876333 MX 6 2,4,7,9-tetraphenyl-1,10- phenanthroline

EP1786050 MX 8 2,9-di(biphenyl-4-yl)-4,7- diphenyl-1,10- phenanthroline

EP1786050 MX 9 4,7-diphenyl-2,9-di-p-tolyl- 1,10-phenanthroline

EP1786050

The electron transport layer may comprises a lithium halide or a lithium organic complex.

Suitable organic ligands to form a lithium organic complex that can be used for the electron transport layer are disclosed, for example in US 2014/0048792 and Kathirgamanathan, Poopathy; Arkley, Vincent; Surendrakumar, Sivagnanasundram; Chan, Yun F.; Ravichandran, Seenivasagam; Ganeshamurugan, Subramaniam; Kumaraverl, Muttulingam; Antipan-Lara, Juan; Paramaswara, Gnanamolly; Reddy, Vanga R., Digest of Technical Papers—Society for Information Display International Symposium (2010), 41(Bk. 1), 465-468.

TABLE 5 Lithium organic complex that can be suitable used for the ETL-layer Refered to as: IUPAC name Structure Reference LiQ lithium 8-hydroxyquinolate

WO 2013079217A1 Li-1 lithium tetra(1H-pyrazol-1- yl)borate

WO 2013079676A1 Li-2 lithium 2-(diphenyl- phosphoryl)phenolate

WO 2013079678A1 Li-3 lithium 2-(pyridin-2- yl)phenolate

JP2 008195623 Li-4 lithium 2-(1-phenyl-1H- benzo[d]imidazol-2- yl)phenolate

JP 2001291593, Li-5 lithium 2-(benzo[d]oxazol-2- yl)phenolate

US 20030165711 Li-6 lithium 2-(diphenyl- phosphoryl)pyridin-3-olate

EP 2724388

The organic ligand of the lithium organic complex of the electron transport layer may be selected from the group comprising a quinolate, a borate, a phenolate, a pyridinolate or a Schiff base ligand, or Table 5;

-   -   preferably the lithium quinolate complex has the formula I:

wherein

-   -   A1 to A6 are same or independently selected from CH, CR, N, O;     -   R is same or independently selected from hydrogen, halogen,         alkyl or aryl or heteroaryl with 1 to 20 carbon atoms; and more         preferred A1 to A6 are CH;     -   preferably the borate based organic ligand is a         tetra(1H-pyrazol-1-yl)borate;     -   preferably the phenolate is a 2-(pyridin-2-yl)phenolate or a         2-(diphenylphosphoryl)phenolate;     -   preferably the lithium Schiff base has the structure 100, 101,         102 or 103:

-   -   more preferred the lithium organic complex is selected from a         compound of Table 5.         The lithium halide of the electron transport layer may be         selected from the group comprising a LiF, LiCl, LiBr or LiJ, and         preferably LiF.

The ETL may be formed on the EML by vacuum deposition, spin coating, slot-die coating, printing, casting, or the like. When the ETL is formed by vacuum deposition or spin coating, the deposition and coating conditions may be similar to those for formation of the HIL 130. However, the deposition and coating conditions may vary, according to a compound that is used to form the ETL.

Substrate

The substrate may be any substrate that is commonly used in manufacturing of organic light-emitting diodes. If light is emitted through the substrate, the substrate may be a transparent material, for example a glass substrate or a transparent plastic substrate, having excellent mechanical strength, thermal stability, transparency, surface smoothness, ease of handling, and waterproofness. If light is emitted through the top surface, the substrate may be a transparent or non-transparent material, for example a glass substrate, a plastic substrate, a metal substrate or a silicon substrate.

Anode Electrode

The anode electrode may be formed by depositing or sputtering a compound that is used to form the anode electrode. The compound used to form the anode electrode may be a high work-function compound, so as to facilitate hole injection. The anode material may also be selected from a low work function material (i.e. Aluminum).The anode electrode may be a transparent or reflective electrode. Transparent conductive compounds, such as indium tin oxide (ITO), indium zinc oxide (IZO), tin-dioxide (SnO₂), and zinc oxide (ZnO), may be used to form the anode electrode 120. The anode electrode 120 may also be formed using magnesium (Mg), aluminum (Al), aluminum-lithium (Al-Li), calcium (Ca), magnesium-indium (Mg—In), magnesium-silver (Mg-Ag), silver (Ag), gold (Au), or the like.

The anode electrode may be formed from a high conductivity metal, for example copper (Cu) or silver (Ag).

The HIL may be formed on the anode electrode by vacuum deposition, spin coating, printing, casting, slot-die coating, Langmuir-Blodgett (LB) deposition, or the like. When the HIL is formed using vacuum deposition, the deposition conditions may vary according to the compound that is used to form the HIL, and the desired structure and thermal properties of the HIL. In general, however, conditions for vacuum deposition may include a deposition temperature of 100° C. to 500° C., a pressure of 10⁻⁸ to 10⁻³ torr (1 torr equals 133.322 Pa), and a deposition rate of 0.1 to 10 nm/sec.

HIL—Forming Conditions

When the HIL is formed using spin coating or printing, coating conditions may vary according to a compound that is used to form the HIL, and the desired structure and thermal properties of the HIL. For example, the coating conditions may include a coating speed of about 2000 rpm to about 5000 rpm, and a thermal treatment temperature of about 80° C. to about 200° C. Thermal treatment removes a solvent after the coating is performed.

HTL—Forming Conditions

The hole transport layer (HTL) may be formed on the HIL by vacuum deposition, spin coating, slot-die coating, printing, casting, Langmuir-Blodgett (LB) deposition, or the like. When the HTL is formed by vacuum deposition or spin coating, the conditions for deposition and coating may be similar to those for the formation of the HIL. However, the conditions for the vacuum or solution deposition may vary, according to the compound that is used to form the HTL.

Emission Layer (EML)

The EML may be formed on the HTL by vacuum deposition, spin coating, slot-die coating, printing, casting, LB, or the like. When the EML is formed using vacuum deposition or spin coating, the conditions for deposition and coating may be similar to those for the formation of the HIL. However, the conditions for deposition and coating may vary, according to the compound that is used to form the EML.

The emission layer (EML) may be formed of a combination of a host and a dopant. Example of the host are Alq3, 4,4′-N,N′-dicarbazole-biphenyl (CBP), poly(n-vinylcarbazole) (PVK), 9,10-di(naphthalene-2-yl)anthracenee (ADN), 4,4′,4″-Tris(carbazol-9-yl)-triphenylamine

(TCTA), 1,3,5-tris(N-phenylbenzimidazole-2-yl)benzene (TPBI), 3-tert-butyl-9,10-di-2-naphthylanthracenee (TBADN), distyrylarylene (DSA), Bis(2-(2-hydroxyphenyl)benzo-thiazolate)zinc (Zn(BTZ) 2), E3 below, AND, Compound 1 below, and Compound 2 below.

The dopant may be a phosphorescent or fluorescent emitter. Phosphorescent emitters are preferred due to their higher efficiency

Examples of a red dopant are PtOEP, Ir(piq) 3, and Btp 2lr(acac), but are not limited thereto. These compounds are phosphorescent emitters, however, fluorescent red dopants could also be used.

Examples of a phosphorescent green dopant are Ir(ppy) 3 (ppy=phenylpyridine), Ir(ppy) 2(acac), Ir(mpyp) 3 are shown below. Compound 3 is an example of a fluorescent green emitter and the structure is shown below.

Examples of a phosphorescent blue dopant are F₂Irpic, (F₂ppy)₂Ir(tmd) and Ir(dfppz) 3, ter-fluorene, the structures are shown below. 4.4′-bis(4-diphenyl amiostyryl)biphenyl (DPAVBi), 2,5,8,11-tetra-tert-butyl perylene (TBPe), and Compound 4 below are examples of fluorescent blue dopants.

The amount of the dopant may be in the range of about 0.01 to about 50 parts by weight, based on 100 parts by weight of the host. The EML may have a thickness of about 10 nm to about 100 nm, for example, about 20 nm to about 60 nm. When the thickness of the EML is within this range, the EML may have excellent light emission, without a substantial increase in driving voltage.

Hole Blocking Layer (HBL)

When the EML comprises a phosphorescent dopant, a hole blocking layer (HBL) may be formed on the EML, by using vacuum deposition, spin coating, slot-die coating, printing, casting, LB deposition, or the like, in order to prevent the diffusion of triplet excitons or holes into the ETL.

When the HBL is formed using vacuum deposition or spin coating, the conditions for deposition and coating may be similar to those for the formation of the HIL. However, the conditions for deposition and coating may vary, according to the compound that is used to form the HBL. Any compound that is commonly used to form a HBL may be used. Examples of compounds for forming the HBL include an oxadiazole derivative, a triazole derivative, and a phenanthroline derivative.

The HBL may have a thickness of about 5 nm to about 100 nm, for example, about 10 nm to about 30 nm. When the thickness of the HBL is within this range, the HBL may have excellent hole-blocking properties, without a substantial increase in driving voltage.

Electron Injection Layer (EIL)

The optional EIL, which may facilitates injection of electrons from the cathode, may be formed on the ETL, preferably directly on the electron transport layer. Examples of materials for forming the EIL include LiF, NaCl, CsF, Li2O, BaO, Ca, Ba, Yb, Mg which are known in the art. Deposition and coating conditions for forming the EIL are similar to those for formation of the HIL, although the deposition and coating conditions may vary, according to a material that is used to form the EIL.

The thickness of the EIL may be in the range of about 0.1 nm to 10 nm, for example, in the range of 0.5 nm to 9 nm. When the thickness of the EIL is within this range, the EIL may have satisfactory electron-injecting properties, without a substantial increase in driving voltage.

Cathode Electrode

The cathode electrode is formed on the EIL if present. The cathode electrode may be a cathode, which is an electron-injecting electrode. The cathode electrode may be formed of a metal, an alloy, an electrically conductive compound, or a mixture thereof. The cathode electrode may have a low work function. For example, the cathode electrode may be formed of lithium (Li), magnesium (Mg), aluminum (Al), aluminum (Al)-lithium (Li), calcium (Ca), barium (Ba), ytterbium (Yb), magnesium (Mg)-indium (In), magnesium (Mg)-silver (Ag), or the like. In addition, the cathode electrode may be formed of a transparent conductive material, such as ITO or IZO.

The thickness of the cathode electrode may be in the range of about 5 nm to 1000 nm, for example, in the range of 10 nm to 100 nm. When the cathode electrode is in the range of 5 nm to 50 nm, the electrode will transparent even if a metal or metal alloy is used.

Since the layers of the ETL have similar or identical energy levels, the injection and transport of the electrons may be controlled, and the holes may be efficiently blocked. Thus, the OLED may have long lifetime.

Light-Emitting Diode (OLED)

According to another aspect of the present invention, there is provided an organic light-emitting diode (OLED) comprising: a substrate; a anode electrode formed on the substrate; a hole injection layer comprising a metal amide according to the invention, a hole transport layer, an emission layer, and a cathode electrode.

According to another aspect of the present invention, there is provided an organic light-emitting diode (OLED) comprising: a substrate; a anode electrode formed on the substrate; a hole injection layer comprising a metal amide according to the invention, a hole transport layer, an emission layer, hole blocking layer and a cathode electrode.

According to another aspect of the present invention, there is provided an organic light-emitting diode (OLED) comprising: a substrate; a anode electrode formed on the substrate; a hole injection layer comprising a charge neutral metal amide according to the invention, a hole transport layer, an emission layer, hole blocking layer, electron transport layer, and a cathode electrode.

According to another aspect of the present invention, there is provided an organic light-emitting diode (OLED) comprising: a substrate; a anode electrode formed on the substrate; a hole injection layer comprising a charge neutral metal amide according to the invention, a hole transport layer, an emission layer, hole blocking layer, electron transport layer, an electron injection layer, and a cathode electrode.

According to another aspect, there is provided an organic light-emitting diode (OLED) comprising: at least one layer selected from the group consisting of a hole injection layer, a hole transport layer, an emission layer, a hole blocking layer, an electron transport layer, exactly in that order between the anode electrode and the cathode electrode.

According to various embodiments of the present invention, there is provided an organic light-emitting diode (OLED) further comprising an electron injection layer formed between the electron transport layer and the cathode electrode.

According to various embodiments of the OLED of the present invention, the OLED may not comprises an electron injection layer.

According to various embodiments of the OLED of the present invention, the OLED may not comprises an electron transport layer.

According to various embodiments of the OLED of the present invention, the OLED may not comprises an electron transport layer and an electron injection layer.

According to another aspect of the present invention, there is provided a method of manufacturing an organic light-emitting diode (OLED), the method using:

-   -   at least one deposition source, preferably two deposition         sources and more preferred at least three deposition sources;         and/or     -   deposition via vacuum thermal evaporation; and/or     -   deposition via solution processing, preferably the processing is         selected from spin-coating, printing, casting and/or slot-die         coating.

Method of Manufacture

According to various embodiments of the present invention, the method may further include forming on the anode electrode an hole injection layer, an hole transport layer, an emission layer and a cathode electrode, exactly in that order.

According to various embodiments of the present invention, the method may further include forming on the anode electrode an hole injection layer, an hole transport layer, an emission layer, an electron transport layer, and a cathode electrode, exactly in that order.

According to various embodiments of the present invention, the method may further include forming on the anode electrode an hole injection layer, an hole transport layer, hole blocking layer, an emission layer, an electron transport layer, and a cathode electrode, exactly in that order.

According to various embodiments of the present invention, the method may further include the steps for forming an organic light-emitting diode (OLED), wherein

-   -   on a substrate a anode electrode is formed,     -   on the anode electrode an hole injection layer is formed,     -   on the hole injection layer an hole transport layer is formed,     -   optional on the hole transport layer a hole blocking layer is         formed,     -   than an emission layer is formed thereon,     -   on the emission layer optional an electron transport layer is         formed, preferably an electron transport layer stack,     -   finally a cathode electrode is formed thereon,     -   optional an electron injection layer is formed between the         electron transport layer and the cathode electrode.

The method of manufacturing the OLED may comprise the steps:

-   -   the hole injection layer according to the invention is deposited         on an anode layer, an optional hole transport layer is deposited         on the hole injection layer, an emission layer is deposited on         the hole transport layer, an optional hole blocking layer is         deposited on the emission layer, an optional electron transport         layer is deposited on the hole blocking layer, an optional         electron injection layer is deposited on the electron transport         layer and a cathode is deposited on the electron injection         layer, wherein the layers are arranged in that order and         sandwiched between the anode and the cathode.

However, according to one aspect the layers are deposited the other way around, starting with the cathode, and sandwiched between the cathode and the anode.

For example, starting with the cathode layer, optional electron injection layer, electron transport layer, optional hole blocking layer, emission layer, hole transport layer, hole injection layer, anode electrode, exactly in this order.

The anode electrode and/or the cathode electrode can be deposit on a substrate. Preferably the anode is deposit on a substrate.

Additional aspects and/or advantages of the invention will be set forth in part in the description which follows and, in part, will be obvious from the description, or may be learned by practice of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

These and/or other aspects and advantages of the present invention will become apparent and more readily appreciated from the following description of the exemplary embodiments, taken in conjunction with the accompanying drawings, of which:

FIG. 1 is a schematic sectional view of an organic light-emitting diode (OLED), according to an exemplary embodiment of the present invention;

FIG. 2 is a schematic sectional view of an OLED, according to an exemplary embodiment of the present invention.

FIG. 3 is a schematic sectional view of an OLED, according to an exemplary embodiment of the present invention.

FIG. 4 is an overview of metal amides based on general Formula Ia that can be used according to the invention.

FIG. 5 is an overview of metal amides that can be used according to the invention with specific A¹ and A², wherein A¹ and A² are SO₂.

FIG. 6 is an overview of metal amides that can be used according to the invention with specific A¹ and A², wherein A¹ and A² are POR⁸.

FIG. 7 is an overview of metal amides that can be used according to the invention with specific A¹ and A², wherein A¹ and A² are CO.

FIG. 8 is an overview of metal amides that can be used according to the invention with specific A¹ and A², wherein A¹ and A² are selected different, wherein A¹ is SO₂ and A² is POR⁸.

DETAILED DESCRIPTION

Reference will now be made in detail to the exemplary embodiments of the present invention, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to the like elements throughout. The exemplary embodiments are described below, in order to explain the aspects of the present invention, by referring to the figures.

Herein, when a first element is referred to as being formed or disposed “on” a second element, the first element can be disposed directly on the second element, or one or more other elements may be disposed there between. When a first element is referred to as being formed or disposed “directly on” a second element, no other elements are disposed there between.

FIG. 1 is a schematic sectional view of an organic light-emitting diode (OLED) 100, according to an exemplary embodiment of the present invention. The OLED 100 includes a substrate 110. On the substrate 110 an anode 120 is disposed. On the anode 120 a hole injection layer 130 containing or consisting of a metal amide compound according to the invention is disposed and thereon a hole transport layer 140. Onto the hole transport layer 140 an emission layer 150 and an cathode electrode 190, exactly in this order, are disposed.

FIG. 2 is a schematic sectional view of an organic light-emitting diode (OLED) 100, according to an exemplary embodiment of the present invention. The OLED 100 includes a substrate 110, a first electrode 120, a hole injection layer (HIL) 130, a hole transport layer (HTL) 140, an emission layer (EML) 150, an electron transport layer (ETL) 161. The electron transport layer (ETL) 161 is formed directly on the EML 150. Onto the electron transport layer (ETL) 161 a cathode electrode 190 is disposed.

Instead of a single electron transport layer 161, optional an electron transport layer stack (ETL) can be used.

FIG. 3 is a schematic sectional view of an OLED 100, according to another exemplary embodiment of the present invention. FIG. 3 differs from FIG. 2 in that the OLED 100 of FIG. 3 comprises a hole blocking layer (HBL) 155 and an electron injection layer (EIL) 180.

Referring to FIG. 3 the OLED 100 includes a substrate 110, an anode electrode 120, a hole injection layer (HIL) 130, a hole transport layer (HTL) 140, an emission layer (EML) 150, a hole blocking layer (HBL) 155, an electron transport layer (ETL) 161, an electron injection layer (EIL) 180 and a cathode electrode 190. The layers are disposed exactly in the order as mentioned before.

In the description above the method of manufacture an OLED of the present invention is started with a substrate 110 onto which an anode electrode 120 is formed, on the anode electrode 120, an hole injection layer 130, hole transport layer 140, an emission layer 150, optional a hole blocking layer 155, optional at least one electron transport layer 161, optional at least one electron injection layer 180, and a cathode electrode 190 are formed, exactly in that order or exactly the other way around.

While not shown in FIG. 1, FIG. 2 and FIG. 3, a sealing layer may further be formed on the cathode electrodes 190, in order to seal the OLEDs 100. In addition, various other modifications may be applied thereto.

Hereinafter, one or more exemplary embodiments of the present invention will be described in detail with, reference to the following examples. However, these examples are not intended to limit the purpose and scope of the one or more exemplary embodiments of the present invention.

EXAMPLES General Procedure

For bottom emission devices, a 15 Ω/cm² glass substrate (available from Corning Co.) with 100 nm ITO was cut to a size of 50 mm×50 mm×0.7 mm, ultrasonically washed with isopropyl alcohol for 5 minutes and then with pure water for 5 minutes, and washed again with UV ozone for 30 minutes, to prepare a first electrode. For top emission devices, the anode electrode was formed from 100 nm silver on glass which was prepared by the same methods as described above.

Then, the hole injection layer, triarylamine compound and charge neutral metal amide compound according to the examples of Table 6 was vacuum co-deposited on the ITO electrode, to form a HIL having a thickness according to the examples 1 to 22 and comparative examples 1 to 5 of tables 6, 7 and 8. Then the corresponding hole injection layer according to the examples 1 to 22 and comparative examples 1 to 5 of tables 6, 7 and 8 was vacuum deposited on the HIL, to form a HTL having a thickness as mentioned in tables 6, 7 and 8, respectively.

The wt.-% of the HIL-compound/s and HTL-compound according to the examples 1 to 22 and comparative examples 1 to 5 can be taken from Tables 6, 7 and 8 below, whereby the wt.-% amount of the HIL-compound/s is 100 wt.-% based on the total weight amount of the HIL-layer, and the wt.-% amount of the HTL-compound/s is 100 wt.-% based on the total weight amount of the HTL-layer, if no not indicated otherwise the wt.-% of the components are indicated in Tables 6, 7 and 8, respectively. That means that the HIL according to examples 1 to 22 consist of the triarylamine compound and metal amide compound according to the invention. However, the hole injection layer may comprises traces of the compound of the hole transport layer, due to the process of manufacture.

97 wt.-% of ABH113 (Sun Fine Chemicals) as a host and 3 wt.-% of NUBD370 (Sun Fine Chemicals) as a dopant were deposited on the HTL, to form a blue-emitting EML with a thickness of 20 nm.

Then the ETL-layer of matrix compound of 50 wt.-% MX 2 and 50 wt.-% LiQ (50 wt.-%:50 wt.-%) having a thickness of 36 nm is formed by deposing the matrix compound from a first deposition source and the lithium organic complex or lithium halide from a second deposition source directly on the EML.

For the comparative examples 1 to 5 and examples 1 to 22 only one electron transport layer is formed.

The cathode was evaporated at ultra-high vacuum of 10⁻⁷ bar. Therefore, a thermal single co-evaporation of one or several metals was performed with a rate of 0, 1 to 10 nm/s (0.01 to 1 Å/s) in order to generate a homogeneous cathode with a thickness of 5 to 1000 nm. For top emission devices, the cathode electrode was formed from 13 nm magnesium (90 vol.-%)-silver (10 vol.-%) alloy. For bottom emission devices, the cathode electrode was formed from 100 nm aluminum.

The OLED stack is protected from ambient conditions by encapsulation of the device with a glass slide. Thereby, a cavity is formed, which includes a getter material for further protection.

To assess the performance of the inventive examples compared to the prior art, the current efficiency is measured under ambient conditions (20° C.). Current voltage measurements are performed using a Keithley 2400 sourcemeter, and recorded in V. At 10 mA/cm² for bottom emission and 15 mA/cm² for top emission devices, a calibrated spectrometer CAS140 from Instrument Systems is used for measurement of CIE coordinates and brightness in Candela. Lifetime LT of the device is measured at ambient conditions (20° C.) and 15 mA/cm², using a Keithley 2400 sourcemeter, and recorded in hours. The brightness of the device is measured using a calibrated photo diode. The lifetime LT is defined as the time till the brightness of the device is reduced to 97% of its initial value.

In bottom emission devices, the emission is predominately Lambertian and quantified in percent external quantum efficiency (EQE). To determine the efficiency EQE in % the light output of the device is measured using a calibrated photodiode at 10 mA/cm².

In top emission devices, the emission is forward directed, non-Lambertian and also highly dependent on the mirco-cavity. Therefore, the efficiency EQE will be higher compared to bottom emission devices. To determine the efficiency EQE in % the light output of the device is measured using a calibrated photodiode at 15 mA/cm².

Technical Effect of the Invention

Effect of the Layer Thickness of the HIL on Device Performance without Cavity Control

In order to test the performance of very thick hole injection layers (HIL), bottom emission OLED-devices are fabricated with a HIL thickness ranging from 100 nm to 450 nm. The HTL thickness is given in Table 6. The cavity, and thereby light out coupling, varies depending on HIL thickness, therefore no data are provided on efficiency EQE. In Table 6 the effect of the HIL thickness without cavity control is shown. As can be seen in Example 1 to 8, only a comparatively small increase in voltage is observed even for very thick layers.

TABLE 6 Effect of HIL thickness on device performance without cavity control HIL dopant HIL HTL HIL dopant concentration thickness thickness U HIL compound [wt.-%] [nm] HTL [nm] [V] Example 1 T-3 Li(TFSI) 2 100 T-3 30 4.7 Example 2 T-3 Li(TFSI) 2 150 T-3 30 4.8 Example 3 T-3 Li(TFSI) 2 200 T-3 30 4.9 Example 4 T-3 Li(TFSI) 2 250 T-3 30 5 Example 5 T-3 Li(TFSI) 2 300 T-3 30 5 Example 6 T-3 Li(TFSI) 2 350 T-3 30 5.1 Example 7 T-3 Li(TFSI) 2 400 T-3 30 5.2 Example 8 T-3 Li(TFSI) 2 450 T-3 30 5.3

Effect of the Layer Thickness of the HIL on Device Performance at Constant Cavity

In Table 7 is shown the effect of the HIL and HTL thickness on performance of bottom emission devices. The thickness of the layers is selected in such a way that the sum of the thickness of HIL and HTL is kept constant at 130 nm. Thereby, the cavity does not change and light outcoupling and efficiency EQE are not impacted.

In comparative examples 1 and 2, the compound CNHAT (CAS 105598-27-4) has been used as a hole injection layer. In comparative example 1, a 10 nm layer of CNHAT was used. The efficiency EQE of 4.9% was obtained at a voltage of 5.4 V. However, it is desired to provide a thick HIL which can smooth over non-uniformities in the anode layer. Therefore, a 100 nm layer of CNHAT was tested. The efficiency EQE of 4.2% was achieved at 4.7 V.

In summary, the efficiency EQE is reduced at thicknesses which would level out non-uniformities.

Example 9 to 15 shows the effect of increased thickness of the HIL comprising triarylamine T-3 and metal amide Li(TFSI) on efficiency, voltage and voltage stability over time. As can be seen in Table 7, the efficiency is always higher than the efficiency obtained for devices containing a CNHAT HIL layer. Additionally, the efficiency EQE remains constant for a HIL thickness ranging from 20 to 120 nm. The voltage for a 20 nm HIL layer is slightly higher compared to the comparative examples but surprisingly, the voltage decreases to 4.8 to 4.9 V for thicker layers (example 10 to 15). The voltage stability of all examples is at an acceptable level, for example less than 0.35V over 50 hours stability test at 15 mA/cm².

TABLE 7 Effect of HIL thickness on device performance at constant cavity HIL dopant HIL HTL U(50 h)- HIL HIL dopant concentration thickness thickness U EQE U(0 h) compound compound [wt.-%] [nm] HTL [nm] [V] [%] [V] Comparative CNHAT 0 10 T-3 120 5.4 4.9 0.06 example 1 Comparative CNHAT 0 100 T-3 30 4.7 4.2 0.01 example 2 Example 9 T-3 Li(TFSI) 2 20 T-3 110 5.1 5.3 0.33 Example 10 T-3 Li(TFSI) 2 40 T-3 90 4.9 5.2 0.16 Example 11 T-3 Li(TFSI) 2 60 T-3 70 4.9 5.2 0.18 Example 12 T-3 Li(TFSI) 2 70 T-3 60 4.8 5.2 0.18 Example 13 T-3 Li(TFSI) 2 80 T-3 50 4.8 5.2 0.18 Example 14 T-3 Li(TFSI) 2 100 T-3 30 4.8 5.2 0.17 Example 15 T-3 Li(TFSI) 2 120 T-3 10 4.8 5.2 0.18

Effect of the Metal Cation on Device Performance

In Table 8, the effect of the metal cation in the metal amide on performance of bottom emission devices. For ease of comparison, a 100 nm HIL was used in all examples. In Examples 16 to 20 are compared triarylamine T-3 doped with Li(TFSI), Ag(TFSI), Mg(TFSI)₂, Mn(TFSI)₂ and Li(cTFSI) (CAS 189217-62-7). The efficiency EQE is always higher than for comparative example 3 with CNHAT. Particularly high efficiency is obtained for a Ag(TFSI) doped HIL (example 18), while the lowest voltage and least voltage increase over time is achieved for Mg(TFSI) and Mn(TFSI)₂ (example 17 and 19, respectively).

Effect of the HOMO Level of the Hole Transport Layer on Device Performance

In order to achieve light output in different colours, a large variety of materials is available for application in the emission layer of OLEDs. Each emission layer composition comes with different demands on the HTL (for example band-gap or triplet level). Therefore, the HTL materials of different OLEDs may differ in their HOMO level. Consequently, a good hole injection layer enables hole injection in to a large variety of HTL materials.

In a second step, triarylamine compounds with deeper HOMO levels are tested in the hole injection layer and hole transport layer, see Table 8. For ease of comparison, a 100 nm HIL was used in all examples. HTLs which show low performance with the fluorescent blue EML used here may show unique performance with a different EML composition, for example phosphorescent blue or green EML, or for TADF (thermally activated delayed fluorescence) emitters. In the following examples, the hole injection performance is evaluated relative to CNHAT which is not suitable for injection into deep HOMO HTLs. In comparative examples 4 and 5, CNHAT HIL is used together with deeper HOMO triarylamine compound T-8 (HOMO −5.25 eV) and T-9 (HOMO −5.33 eV). Compared to comparative example 3, where a triarylamine compound with a HOMO closer to vacuum level was used (T-3, HOMO −5.10 eV), the efficiency is slightly increased, however the voltage is so high, that a commercial application cannot be considered. As the voltage is very high, the voltage stability over time has not been measured. In example 21 and 22, the effect of a HIL comprising deep HOMO triarylamines and metal amide Mg(TFSI) is evaluated. As can be seen in Table 8, the efficiency is significantly higher than for CNHAT HIL and the voltage is significantly lower (5.2 compared to 6.1 V and 6.2 compared to 8.6 V, respectively). In summary, a wide range of metal amides with various metal cations can be successfully used as HIL dopant. Additionally, both open-chain and cyclic amide ligands show the desired effect (Li(TFSI) compared to Li(cTFSI), example 16 and 20, respectively). Furthermore, the invention is particularly useful for efficient hole injection into deeper HOMO HTLs which are required for OLEDs which rely on phosphorescent or TADF emitters, in particular green and blue emitters.

TABLE 8 Effect of metal cation and HOMO level of HTL on device performance HIL dopant HIL U(50 h)- HIL HIL dopant concentration Thickness U EQE U(0 h) compound compound [wt.-%] [nm] HTL [V] [%] [V] Comparative CNHAT — 0 100 T-3 4.7 4.2 0.01 example 3 Comparative CNHAT — 0 100 T-8 6.1 4.5 — example 4 Comparative CNHAT — 0 100 T-9 8.6 4.9 — example 5 Example 16 T-3 Li(TFSI) 2 100 T-3 4.8 5.2 0.17 Example 17 T-3 Mg(TFSI)₂ 2 100 T-3 4.8 5.1 0.02 Example 18 T-3 Ag(TFSI) 2 100 T-3 5.6 5.3 0.2 Example 19 T-3 Mn(TFSI)₂ 2 100 T-3 4.7 4.7 0.14 Example 20 T-3 Li(cTFSI) 2 100 T-3 4.8 4.9 0.15 Example 21 T-8 Mg(TFSI)₂ 2 100 T-8 5.2 5.3 0.1 Example 22 T-9 Mg(TFSI)₂ 2 100 T-9 6.2 5.3 0.25

Another aspect is directed to an organic light-emitting diode (OLED) comprising more than one emission layer (EML) 150, for example two, three or four emission layers may be present. An organic light-emitting diode (OLED) comprising more than one emission layer is also described as a tandem OLED or stacked OLED.

Another aspect is directed to a device comprising at least one organic light-emitting diode (OLED). A device comprising organic light-emitting diodes (OLED) is for example a display or a lighting panel.

From the foregoing detailed description and examples, it will be evident that modifications and variations can be made to the compositions and methods of the invention without departing from the spirit and scope of the invention. Therefore, it is intended that all modifications made to the invention without departing from the spirit and scope of the invention come within the scope of the appended claims. 

1. A hole injection layer for an OLED comprising a triarylamine compound (VIIa) doped with a charge neutral metal amide compound (Ia), characterized in that the hole injection layer has a thickness of at least about ≥20 nm to about ≤1000 nm and the charge neutral metal amide compound has the Formula Ia:

wherein: G=halide, O, alkoxylate or amine of Formula Ha to He:

R¹ to R⁵ are independently selected from the group comprising H, C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to C₁₂ substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂ substituted heteroaryl with 5 to 20 ring-forming atoms, halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated heteroaryl with 5 to 20 ring-forming atoms; or at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵ are bridged and form a 5 to 20 member ring; m=0, 1, 2, 3 or 4; M=a metal selected from the group comprising alkali metal, alkaline earth metal, Al, Ga, In, transition metal or rare earth metal; wherein the bond between N and the metal M is a covalent bond or N forms a non-covalent interaction to the metal M; L=charge neutral ligand which coordinates to the metal M, selected from the group comprising H₂O, C₂ to C₄₀ mono- or multi-dentate ethers and C₂ to C₄₀ thioethers, C₂ to C₄₀ amines, C₂ to C₄₀ phosphine, C₂ to C₂₀ alkyl nitrile or C₂ to C₄₀ aryl nitrile, or a compound according to Formula (III);

wherein R⁶ and R⁷ are independently selected from C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, C₆ to C₂₀ aryl, heteroaryl with 5 to 20 ring-forming atoms, halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated heteroaryl with 5 to 20 ring-forming atoms, or at least one R⁶ and R⁷ are bridged and form a 5 to 20 member ring, or the two R⁶ and/or the two R⁷ are bridged and form a 5 to 40 member ring or form a 5 to 40 member ring comprising an unsubstituted or C₁ to C₁₂ substituted phenanthroline; p=0, 1, 2 or 3; A¹, A², A³ and A⁴ are independently selected from CO, SO₂ or POR⁸; R⁸=electron withdrawing group selected from the group comprising halide, nitrile, halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or perhalogenated C₆ to C₂₀ aryl, or halogenated or perhalogenated heteroaryl with 5 to 20 ring-forming atoms; n=1, 2, 3, 4 or 5; B¹, B², B³ and B⁴ are same or independently selected from substituted or unsubstituted C₁ to C₂₀ alkyl, substituted or unsubstituted C₁ to C₂₀ heteroalkyl, substituted or unsubstituted C₆ to C₂₀ aryl, substituted or unsubstituted C₅ to C₂₀ heteroaryl, or B¹ and B² are bridged; wherein B¹ and B² are bridged, then: M, N, A¹, B¹, B², A² and N form a 7 to 10 member ring according to Formula Ib;

 or N, A¹, B¹, B² and A² form a 5 to 10 member ring according to Formula Ic,

 or N, A¹, B¹, B² and A² form a first 5 to 10 member ring and B¹ and B² form a second 5 to 20 member ring according to Formula Id:


2. The hole injection layer according to claim 1, wherein the triarylamine compound has the Formula VIIa:

wherein: Ar¹ and Ar²=independently selected from substituted or unsubstituted C₆ to C₂₀ arylene; Ar³ and Ar⁴=independently selected from substituted or unsubstituted C₆ to C₂₀ aryl; Ar⁵ and Ar⁶=independently selected from substituted or unsubstituted C₆ to C₂₀ aryl or C₅ to C₄₀ heteroaryl; R⁹=a single chemical bond, a unsubstituted or substituted C₁ to C₆ alkyl and unsubstituted or substituted C₁ to C₅ heteroalkyl; q=0, 1 or 2; r=0 or 1; wherein the substituents for Ar¹ to Ar⁶ are independently selected from C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, or halide; and the substitutents for R⁹ are independently selected from C₁ to C₆ alkyl, C₁ to C₅ heteroalkyl, C₆ to C₂₀ aryl and C₅ to C₂₀ heteroaryl; wherein the charge neutral metal amide compound has the Formula Ia, Ib, Ic or Id.
 3. The hole injection layer according to claim 1, wherein: the hole injection layer comprises one triarylamine compound; or the hole injection layer comprises one charge neutral metal amide compound; or the hole injection layer comprises one triarylamine compound and one charge neutral metal amide compound.
 4. The hole injection layer according to claim 1, wherein the charge neutral metal amide compound has the Formula Ia,

wherein: A¹ and A² are same or independently selected from CO, POR⁸ and SO₂; or A¹ and A² are independently selected from CO, POR⁸, SO₂, and N, A¹, B¹, A² and B² form a 5 to 10 member ring.
 5. The hole injection layer according to claim 1, wherein for: p=0, m=1, 2, 3 or 4 and n=1, 2, 3 or 4, the charge neutral metal amide compound has the Formula IIa:

 or p=1, 2 or 3, and n=1, 2, 3 or 4 and m=0, the charge neutral metal amide compound has the Formula IIb:

 or p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, B¹, B² and A² form a 5 to 10 member ring, the charge neutral metal amide compound has the Formula IIc:

 or p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, A¹, B¹, B² and A² form a first 5 to 10 member ring and B¹ and B² are bridged to form a second 5 to 20 member ring, the charge neutral metal amide compound has the Formula IId:

 or p=1, 2 or 3, n=1, m=1, 2, 3 or 4, and M, N, A¹, B¹, B², A² and N form a 7 to 10 member ring, the charge neutral metal amide compound has the Formula IIe:

p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, A¹, B¹, B² and A² form a 5 to 10 member ring, the charge neutral metal amide compound has the Formula IIf:

p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, A¹, B¹, B² and A² form a first 5 to 10 member ring, and B¹ and B² are bridged to form a second 5 to 20 member ring, the charge neutral metal amide compound has the Formula IIg:

p=1, 2 or 3, n=1, m=0 and M, N, A¹, B¹, B², A² and N form a 7 to 10 member ring, the charge neutral metal amide compound has the Formula IIh:


6. The hole injection layer according to claim 1, wherein for A¹ and A² are SO₂: p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4, the charge neutral metal amide compound has the Formula IIIa:

p=0, n=1, 2, 3 or 4, m=1, 2, 3 or 4, the charge neutral metal amide compound has the Formula IIIb:

p=1, 2 or 3, n=1, 2, 3 or 4, m=0, the charge neutral metal amide compound has the Formula IIIc:

p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, SO₂, B¹, B² and SO₂ form a 5 to 10 member ring, the charge neutral metal amide compound has the Formula IIId:

p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, SO₂, B¹, B² and SO₂ form a first 5 to 10 member ring, and B¹ and B² are bridged to form a second 5 to 20 member ring, the charge neutral metal amide compound has the Formula IIIe:

p=1, 2 or 3, n=1, m=1, 2, 3 or 4 and M, N, SO₂, B¹, B², SO₂ and N form a 7 to 10 member ring, the charge neutral metal amide compound has the Formula IIIf:

p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, SO₂, B² and SO₂ form a 5 to 10 member ring, the charge neutral metal amide compound has the Formula IIIg:

p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, SO₂, B¹, B² and SO₂ form a first 5 to 10 member ring, and B¹ and B² are bridged to form a second 5 to 20 member ring, the charge neutral metal amide compound has the Formula IIIh:

p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and M, N, SO₂, B¹, B², SO₂ and N form a 7 to 10 member ring, the charge neutral metal amide compound has the Formula IIIi:

wherein for A¹ and A² are POR⁸: p=1, 2 or 3, m=1, 2, 3 or 4 and n=1, 2, 3 or 4, the charge neutral metal amide compound has the Formula IVa:

p=0, m=1, 2, 3 or 4 and n=1, 2, 3 or 4, the charge neutral metal amide compound has the Formula IVb:

p=1, 2 or 3, m=0 and n=1, 2, 3 or 4, the charge neutral metal amide compound has the Formula IVc:

p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, POR⁸, B¹, B² and POR⁸ forma 5 to 10 member ring, the charge neutral metal amide compound has the Formula (IVd):

p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, POR⁸, B¹, B² and POR⁸ form a 5 to 10 member ring, the charge neutral metal amide compound has the Formula (IVe):

wherein for A¹ and A² are CO: p=1, 2 or 3, m=1, 2, 3 or 4 and n=1, 2, 3 or 4, the charge neutral metal amide compound has the Formula Va:

p=0, n=1, 2, 3 or 4, m=1, 2, 3 or 4, the charge neutral metal amide compound has the Formula Vb:

p=1, 2 or 3, n=1, 2, 3 or 4, m=0, the charge neutral metal amide compound has the Formula Vc:

p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, CO, B¹, B² and CO form a 5 to 10 member ring, the charge neutral metal amide compound has the Formula Vd:

p=1, 2 or 3, n=1, 2, 3 or 4, m=1, 2, 3 or 4 and N, CO, B¹, B² and CO form a first 5 to 10 member ring, and B¹ and B² are bridged to form a second 5 to 20 member ring, the charge neutral metal amide compound has the Formula Ve:

p=1, 2 or 3, n=1, m=1, 2, 3 or 4 and M, N, CO, B¹, B², CO and N form a 7 to 10 member ring, the charge neutral metal amide compound has the Formula Vf:

p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, CO, B¹, B² and CO form a 5 to 10 member ring, the charge neutral metal amide compound has the Formula (Vg):

p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and N, CO, B¹, B² and CO forma first 5 to 10 member ring, and B¹ and B² form a second 5 to 20 member ring, the charge neutral metal amide compound has the Formula Vh:

p=1, 2 or 3, n=1, 2, 3 or 4, m=0 and M, N, CO, B¹, B², CO and N form a 7 to 10 member ring, the charge neutral metal amide compound has the Formula (Vi):

 or wherein for A¹ is SO₂ and A² is POR⁸: p=1, 2 or 3, m=1, 2, 3 or 4 and n=1, 2, 3 or 4, the charge neutral metal amide compound has the Formula VIa:


7. The hole injection layer according to claim 1, wherein B¹, B², B³ and B⁴ are independently selected from a substituted C₁ to C₂₀ alkyl, substituted C₁ to C₂₀ heteroalkyl, substituted C₆ to C₂₀ aryl, or substituted Cs to C₂₀ heteroaryl; wherein the substituent is an electron withdrawing group selected from the group comprising a halide, nitrile, perhalogenated C₁ to C₂₀ alkyl, perhalogenated C₆ to C₂₀ aryl, perhalogenated heteroaryl with 6 to 20 ring-forming atoms.
 8. The hole injection layer according to claim 1, wherein m=0, 1 or
 2. 9. The hole injection layer according to claim 1, wherein M is selected from Li(I), Na(I), K(I), Cs(I), Mg(II), Ca(II), Sr(II), Ba(II), Sc(III), Y(III), Ti(IV), V(III-V), Cr(III-VI), Mn(II), Mn(III), Fe(II), Fe(III), Co(II), Co(III), Ni(II), Cu(I), Cu(II), Zn(II), Ag(I), Au(I), Au(III), Al(III), Ga(III), In(III), Sn(II), Sn(IV), or Pb(II).
 10. The hole injection layer according to claim 1, wherein the charge neutral metal amide compound has the Formula Ib:

wherein A³ and A⁴ are same or independently selected from CO, POR⁸ or SO₂; B³ and B⁴ are independently selected from substituted or unsubstituted C₁ to C₂₀ alkyl, substituted or unsubstituted C₁ to C₂₀ heteroalkyl, substituted or unsubstituted C₆ to C₂₀ aryl, substituted or unsubstituted C₆ to C₂₀ heteroaryl; and M, N, A¹, B¹, A² and B² form a 7 to 10 member ring.
 11. The hole injection layer according to claim 1, wherein N, A¹, B¹, A² and B² form a first 5 to 10 member ring and B¹ and B² according to Formula Id:

are bridged to form a second ring of a substituted or unsubstituted C₆ to C₂₀ aryl, or of a substituted or unsubstituted C₆ to C₂₀ heteroaryl ring.
 12. The hole injection layer according to claim 1, wherein the charge neutral metal amide compound is selected from at least one of the fluorinated compounds according to Formula C1 to C25: wherein Formula C1 to C16, wherein p=0, m=0, n=1, 2, 3 or 4 and A¹ and A² are SO₂:

Formula C17 to C23, wherein n=1, 2, 3 or 4, A¹ and A² are CO:

Formula C24 to C25, wherein n=1, 2, 3 or 4, A¹ and A² are POR⁸:


13. The hole injection layer according to claim 1, wherein the charge neutral metal amide compound is selected from at least one fluorinated compound according to Formula D1 to D24: wherein p=0, m=0, n=1, 2, 3 or 4 and A¹ and A² are SO₂:


14. The hole injection layer according to claim 1, wherein the charge neutral metal amide compound is selected from at least one fluorinated compound according to Formula F1 to F23: wherein the charge neutral ligand L coordinates to the metal M:

wherein R⁶ and R⁷ are independently selected from C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, C₆ to C₂₀ aryl, heteroaryl with 5 to 20 ring-forming atoms, halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated heteroaryl with 5 to 20 ring-forming atoms, or at least one R⁶ and R⁷ are bridged and form a 5 to 20 member ring, or the two R⁶ and/or the two R⁷ are bridged and form a 5 to 40 member ring or form a 5 to 40 member ring comprising an unsubstituted or C₁ to C₁₂ substituted phenanthroline.
 15. The hole injection layer according to claim 1, wherein the charge neutral metal amide compound is selected from at least one fluorinated compound according to Formula F24 to F45: wherein a halide, O, alkoxylate or amine bonds to the metal M:

wherein R¹ to R⁵ are independently selected from the group comprising H, C₁ to C₂₀ alkyl, C₁ to C₂₀ heteroalkyl, unsubstituted or C₁ to C₁₂ substituted C₆ to C₂₀ aryl, unsubstituted or C₁ to C₁₂ substituted heteroaryl with 5 to 20 ring-forming atoms, halogenated or perhalogenated C₁ to C₂₀ alkyl, halogenated or perhalogenated C₁ to C₂₀ heteroalkyl, halogenated or perhalogenated C₆ to C₂₀ aryl, halogenated or perhalogenated heteroaryl with 5 to 20 ring-forming atoms; or at least one R¹ and R⁴ and/or R² and R³ and/or R¹ and R⁵ are bridged and form a 5 to 20 member cyclic ring.
 16. The hole injection layer according to claim 1, wherein for the triarylamine compound having the Formula VIIa: Ar¹ and Ar² are independently selected from phenylene, biphenylene, naphthylene, anthranylene, carbazolylene and fluorenylene; Ar³ to Ar⁶ are independently selected from phenyl, biphenyl, terphenyl, quartphenyl, fluorenyl, napthyl, anthranyl, phenanthryl, thiophenyl, fluorenyl, 9-carbazolyl.
 17. The hole injection layer according to claim 1, wherein the triarylamine compound has the Formula VIIb to VIIk:


18. (canceled)
 19. (canceled)
 20. (canceled)
 21. An OLED according to claim 1, comprising: an anode, a hole injection layer and an emission layer, wherein the hole injection layer is in direct contact with the anode and the emission layer is in direct contact with the hole injection layer.
 22. (canceled)
 23. An OLED according to claim 1, comprising: an anode, a hole injection layer, a hole transport layer and an emission layer, wherein the hole injection layer is in direct contact with the anode and the hole transport layer is in direct contact with the hole injection layer; and wherein the composition of the hole injection layer is different to the composition of the hole transport layer. 